Abstract:In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe2O4 and ferrimagnetic oxide/ferromagnetic metal CoFe2O4/CoFe2 nanocomposites. The latter compound is a good system to study hard ferrimagnet/soft ferromagnet exchange coupling. Two steps were used to synthesize the bimagnetic CoFe2O4/CoFe2 nanocomposites: (i) first preparation of CoFe2O4 nanoparticles using the a simple hydrothermal method and (ii) second reduction reaction of cobalt ferrite nanoparticles using activated charcoal in inert atmosphere and high temperature. The phase structures, particle sizes, morphology, and magnetic properties of CoFe2O4 nanoparticles have been investigated by X-Ray diffraction (XRD), Mossbauer spectroscopy (MS), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM) with applied field up to 3.0 kOe at room temperature and 50K. The mean diameter of CoFe2O4 particles is about 16 nm. Mossbauer spectra reveal two sites for Fe3+. One site is related to Fe in an octahedral coordination and the other one to the Fe3+ in a tetrahedral coordination, as expected for a spinel crystal structure of CoFe2O4. TEM measurements of nanocomposite show the formation of a thin shell of CoFe2 on the cobalt ferrite and indicate that the nanoparticles increase to about 100 nm. The magnetization of nanocomposite showed hysteresis loop that is characteristic of the exchange spring systems. A maximum energy product (BH)max of 1.22 MGOe was achieved at room temperature for CoFe2O4/CoFe2 nanocomposites, which is about 115% higher than the value obtained for CoFe2O4 precursor. The exchange-spring interaction and the enhancement of product (BH)max in nanocomposite CoFe2O4/CoFe2 have been discussed.

Exchange bias effect and exchange spring-type behavior of core-shell structured MnFe2O4/α-Fe2O3 nanocomposite systems

A study of exchange bias effect in Fe3O4/MnO core–shell hetero-nanostructures

Exchange-spring behavior in bimagnetic CoFe2O4/CoFe2 nanocomposite

Exchange bias induced by CoMn2O4 interface grown through sequential annealing in Mn2O3@Co3O4 core–shell nanocomposite

Exchange Bias Effect and Magnetic Properties in ${\Hbox{la}}_{0.7}{\hbox{sr}}_{0.3}{\hbox{mno}}_{3}\hbox{-}{\Hbox{nio}}$ Nanocomposite Films

Exchange bias and exchange spring in CoFe2O4/FeO/CoFe nanocomposites

Exchange Bias Effect in Nio/Nife2o4 Nanocomposites

Exchange Bias in LiNi0.5Mn1.5O4–NiO Nanocomposites

Exploring the Enhancement of Exchange Bias in α-Fe2O3/g-C3N4 Composites:Synthesis, Magnetic Properties and a First-order Reversal Curve Analysis

Observation of the exchange spring behavior in hard–soft-ferrite nanocomposite

Connection Between Intrinsic Interfacial Frozen Spins and Exchange Bias Effect in Core@Shell Iron@Iron‐Oxide Nanoparticles

The Exchange Bias Effect of CoFe2O4@NiO Core–Shell Nanofibers Based on Annealing Temperature

Ferromagnetic/antiferromagnetic Exchange Coupling in Melt-Spun NdFeB Nanocomposites

Exchange Bias Effect in LaFeO3: La0.7Ca0.3MnO3 Composite Thin Films

Dependence of Exchange Bias on Interparticle Interactions in Co/CoO Core/shell Nanostructures

Exchange bias in CrN/Co nanocomposites consisting of CrN-coated Co nanocapsules and CrN nanoparticles

Exchange Bias in Fe and Ni Codoped CuO Nanocomposites

Crosscaps in Gepner Models and the Moduli space of T2 Orientifolds

Ferromagnetic/antiferromagnetic Exchange Coupling in SrFe 12 O 19 /coo Composites

Exchange Bias in a Core/shell Magnetic Nanoparticle: Monte Carlo Simulation

Utilizing the Anti-Ferromagnetic Functionality of A Multiferroic Shell to Study Exchange Bias in Hybrid Core-Shell Nanostructures