Magnetoelectric composites of lead-free piezoelectrics and yttrium iron garnet: interfacial reactions and functional properties

I. V. Lisnevskaya,I. A. Aleksandrova

DOI: https://doi.org/10.1007/s00339-020-03602-6

2020-05-11

Applied Physics A

Abstract:A wide range of magnetoelectric composites has been prepared: (100 − <i>x</i>) wt% FE + <i>x</i> wt% YIG (<i>x</i> = 30–70 in steps of 10 wt%), where YIG is yttrium iron garnet and FE is a lead-free ferroelectric material reported in the literature, namely lithium sodium potassium niobate ([Li_0.06(Na_0.52K_0.48)]_1.04NbO₃, KLNN), modified sodium bismuth titanate ([96 mol.% Bi_0.5(Na_0.84K_0.16)_0.5TiO₃ + 4 mol.% SrTiO₃ + 0.2 wt% La₂O₃], BNT) or barium calcium zirconate titanate (Ba_0.85Ca_0.15Ti_0.9Zr_0.1O₃, BCZT). The interfacial reactions and dielectric, piezoelectric, magnetic and magnetoelectric behaviors of the composites have been studied. The high-temperature calcination was found to yield the fergusonite-type impurity phase YNbO₄ in KLNN-containing composites and the pyrochlore-like phase Y₂Ti₂O₇ in BNT-containing ones. The BCZT-containing samples remain the only phase-pure materials after heat treatment. As a result, among the materials studied, the samples of (100 − <i>x</i>) wt% BCZT + <i>x</i> wt% YIG show the best magnetoelectric coupling coefficient Δ<i>E</i>/Δ<i>H</i> that reaches ~ 5 mV/(cm Oe) with <i>x</i> = 40. Despite showing significant piezoelectric response, the KLNN-containing ceramics exhibit Δ<i>E</i>/Δ<i>H</i> of 1.2 mV/(cm Oe) or less. The composites containing BNT show weak piezoelectric and almost zero ME response (Δ<i>E</i>/Δ<i>H</i> does not exceed 0.2 mV/(cm Oe)) due to the decomposition of ferroelectric phase caused by high-temperature interfacial reactions. The BCZT-containing composites appeared to be magnetically softer than KLNN-containing materials and magnetically harder than BNT-containing ones.