Abstract:High intensity nanosecond laser pulses induce damage on uncoated optics and antireflection (AR) coated optics with thin film boundaries. Structured surfaces with AR performance have shown higher damage resistance than conventional AR coatings. This work explores laser-induced damage threshold (LIDT) of random antireflective surface structures (rARSS), covering interfaces of planar fused silica substrates, using a 7 ± 1 nanosecond duration, single damaging pulse at 1064-nm wavelength. The rARSS treated windows were optimized for AR at 1064 nm, and transmittance of each treated interface was increased by 3.2% per ISO 13697. Incident fluence was controlled near LIDT for both entry and exit sides. Multiple locations were tested for each fluence setting in accordance with ISO 21254 1-on-1 LIDT testing. Double-sided and single-sided rARSS, orientation with both entrance-side and exit-side treatments, were tested to determine effects random structures have in damage induced by field enhancement on the exit side. Results show that rARSS on a single side of an optic have higher resistance to onset of laser damage when located at entry (structured) side. All tests resulting in damage of polished and single-sided rARSS oriented on exit side were ballistic on beam exit facet, showing surface cracks. Results from rARSS located on beam entry side (both single- and double-side treated) showed nonballistic damage and densification of rARSS features from localized melting or reflow, capping the rARSS but still preserving effective-gradient index and rARSS transmission enhancement. This suggests that the localized melting of the rARSS optic surface does not constitute damage optically, or at least not catastrophically within the prebulk damage regime. Therefore, it is possible to foresee the onset of true damage within an optical system via tracking transmission drop, and swap optics out before catastrophic system failure. The drop in transmission acts as an early warning system, making these rARSS optics an invaluable tool in high-energy laser development.

Experimental Study on the Damage of Optical Materials by out of Band Composite Laser

Researches on Laser Damage Resistance of Optical Films

Damage characteristics of 193 nm laser irradiated on MgF2 window

Study of Damage in Germanium Optical Window Irradiated by a Near-infrared Continuous Wave Laser

Design and Comparison of Laser Windows for High-Power Lasers

Thermodynamic damage behavior of single-crystal MgF2 irradiated by high-power fiber laser

Numerical Analysis of the Thermal and Mechanical Effects of Laser Windows of a High-Power All-Solid-state 2-Μm Laser System

Theoretical and Experimental Study of Laser Induced Damage on Gaas by Nanosecond Pulsed Irradiation

Laser damage of optical windows with random antireflective surface structures on both interfaces

Laser damage of silica optical windows with random antireflective structured surfaces

Laser-induced Damage in a Silicon-Based Photodiode by MHz Picosecond Laser

Laser-induced damage properties of antireflective porous glasses

Laser Induced Damage of Optical Elements–a Status Report

Laser-induced damage and defect analysis of calcium fluoride window caused by the high pulse repetition rate of ArF excimer laser radiation

Simulation study on laser damage threshold of optical window materials

Damage morphology and mechanism in ablation cutting of thin glass sheets with picosecond pulsed lasers

Investigation on Damage Process of Gaas Induced by 1064 Nm Continuous Laser

Pulsed HF/DF Laser Damage in Window Materials.

Effect of microstructure on thermal field distribution of absorption glass with nanosecond laser-irradiated

Laser induced damage studies in borosilicate glass using nanosecond and sub nanosecond pulses

ArF laser-induced damage of calcium fluoride windows with protected anti-reflection coatings