High-flux loose nanofiltration membrane with anti-dye fouling ability based on TA@ZIF-8 for efficient dye/salt separation
Chunmei Gao,Peng Zou,Shifeng Ji,Yunqing Xing,Jiaonan Cai,Jinjian Wu,Tianyang Wu
DOI: https://doi.org/10.1016/j.jece.2023.110444
IF: 7.7
2023-07-09
Journal of Environmental Chemical Engineering
Abstract:Herein, we report a preparation method based on a modified zeolite imidazolate skeleton loose nanofiltration membrane used to achieve the efficient separation of salt and dye from dye wastewater. In this study, negatively charged hydrophilic was synthesized using a tannin surface-functionalization-assisted etching process by tannic acid (TA). A novel, highly negatively charged, and loose nanofiltration membrane was then prepared by adding to a polyethyleneimine (PEI) and tricarboxylic acid (TMA) crosslinking system. The addition of nanoparticles not only changed the degree of crosslinking of PEI/TMA but also provided a preferential channel for water molecules, thereby improving the flux of the membrane. Then, the success of NPs and membranes preparation were verified by SEM, XRD, FT-IR, TGA , BET, XPS and other methods. The results showed that the optimal preparation conditions were 0.020 wt% loading, and the contact angle of the membranes decreased from 79.8° to 53.7°. The water flux of the membrane is 81 L·m −2 ·h −1 ·bar −1 , which is 1.5 times that of PEI/TMA membrane. In addition, –2 membrane not only has high rejection rate for Methyl blue (98.7 %), Toluidine blue (89.6 %), Cr 6+ (91.2 %), but also maintains high transmittance for NaCl and Na 2 SO 4 . Besides, the separation performance of the membrane was stable for a long time in a mixed solution of dye and salt and excellent antifouling performance. Therefore, the loose /PEI/TMA nanofiltration membrane has broad application prospects in printing and dyeing wastewater treatments.
engineering, chemical, environmental