A new perspective on hydrogen diffusion and hydrogen embrittlement in low-alloy high strength steel

X.Y. Cheng,H.X. Zhang
DOI: https://doi.org/10.1016/j.corsci.2020.108800
IF: 7.72
2020-09-01
Corrosion Science
Abstract:Hydrogen diffusion and hydrogen induced embrittlement have been studied in low-alloyed high strength steel tempered at three different temperature using electrochemical permeation and mechanical tensile tests, respectively. After multiple hydrogen trap sites around dislocation core was first proposed, the quantitative relations between hydrogen diffusivity, hydrogen concentration, as well as activation energy for hydrogen diffusion and hydrogen trap sites density were developed. In addition, the hydrogen induced embrittlement would result from higher trap density and higher hydrogen concentration. Hence the connection among hydrogen diffusion, microstructure and hydrogen induced embrittlement were established where the hydrogen trap sites density served as a bridge.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?