Coating of bioactive glasses with chitosan: The effects of the glass composition and coating method on the surface properties, including preliminary in vitro results
S. Spriano,G. Riccucci,G. Örlygsson,C.H. Ng,E. Vernè,F.P. Sehn,P.T. de Oliveira,S. Ferraris
DOI: https://doi.org/10.1016/j.surfcoat.2023.129824
IF: 4.865
2023-07-29
Surface and Coatings Technology
Abstract:Two bioactive glasses were coated with chitosan: SCNB belongs to the SiO 2 -CaO-Na 2 O system, and SCNA has the addition of Al 2 O 3 to enhance chemical stability. Different coating methods were compared: direct physical attachment, surface activation through tresyl chloride, and polydopamine as a linker. The samples were characterized through SEM-EDS, contact angle measurements, FTIR, zeta potential titrations, tape tests, in vitro precipitation of hydroxylapatite (bioactivity), and cell cultures (RAW 264.7 and UMR-106) on some selected samples. Direct physical attachment (in acetic acid) or use of polydopamine allowed complete surface coverage, while it dropped to one-quarter on both glasses by using tresyl chloride. The coating had a contact angle of about 80° and it well showed typical functional groups (FTIR). The coatings on SCNA were chemically and mechanically stable (classified as 4-5B by the tape tests, partially maintained after soaking for 14 days), and showed an isoelectric point around 8. On SCNB, the coatings were unstable (classified as 0-3B, dissolved during soaking) but bioactivity was preserved. The coating affected the biological outcome of SCNA with M0/M1 polarization (1 day) and reduced viability of macrophages (3 days), while osteoblastic cells showed poor adhesion but maintained cell viability and osteogenic potential (3–7 days).
physics, applied,materials science, coatings & films