Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Bio-oil-based phenol–formaldehyde resin: comparison of weight- and molar-based substitution of phenol with bio-oil

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis and Properties of a Novel Bio-based Benzoxazine

Green Phenolic Resins from Oil Palm Empty Fruit Bunch (EFB) Phenolated Lignin and Bio-Oil as Phenol Substitutes for Bonding Plywood

Bio-oil As Substitute of Phenol for Synthesis of Resol-type Phenolic Resin As Wood Adhesive

Use of Biocrude Derived from Woody Biomass to Substitute Phenol at a High‐substitution Level for the Production of Biobased Phenolic Resol Resins

Thermal Stabilities of Phenolic Resoles Prepared from Four Phenolic Compounds as Model Components of Bio‐Oil

Aging Behaviors of Phenol-Formaldehyde Resin Modified by Bio-Oil under Five Aging Conditions

Use Of Hydroxymethylated Lignin In Phenol-Formaldehyde Resins

Synthesis and regulation mechanism of bio-oil–glucose phenolic resin using furfural as cross-linking agent

Neutrals influence on the water resistance coefficient of phenol-formaldehyde resin modified by wood pyrolysis liquid products

Eucalyptus Bark as Source of Bio-oil or Phenolic Compounds

Lignin Phenol Formaldehyde Resoles Using Base-Catalysed Depolymerized Kraft Lignin

Preparation and Characterization of Date Palm Bio-Oil Modified Phenolic Foam

Multispectroscopic Analysis in the Synthesis of Lignin-Based Biophenolic Resins

Preparation of Biobased High Ortho Novolak Resin

Preparation of Phenolic Foam Plastics Based on Fast Paralytic Oil of Biomass

Techno‐economic analysis of novolac resin production by partial substitution of petroleum‐derived phenol with bio‐oil phenol

Elucidation of the effect of fast pyrolysis and hydrothermal liquefaction on the physico-chemical properties of bio-oil from southern yellow pine biomass as a chemical feedstock

Preparation and Characterization of Phenol-Formaldehyde Resins Modified with Alkaline Rice Straw Lignin

Preparation and Characterization of a Phenol-formaldehyde Resin Adhesive Obtained from Bio-ethanol Production Residue