Abstract:Pristine tin selenide and copper doped SnSe single crystals are grown by direct vapour transport technique. X‐ray diffraction and Raman analysis confirm the single SnSe phase having an orthorhombic unit cell. Cu doping in SnSe is also observed by shifting of X‐ray diffraction and Raman peaks of SnSe. The electrical conductivity, thermal conductivity, carrier concentration, Seebeck coefficient and Figure of merit of grown SnSe single crystals are highly optimized by Cu doping in SnSe which makes it a potential candidate in the fabrication of thermoelectric devices. Pristine tin selenide (SnSe) and copper (Cu) doped SnSe single crystals are grown by direct vapour transport technique. The energy dispersive X‐ray, X‐ray diffraction and Raman spectroscopic analysis of grown crystals show preferred stoichiometry having a single phase othorhombic SnSe. The electrical conductivity of SnSe and Cu doped SnSe are 24.24 and 106.06 S m−1 at 310 K respectively which increase as temperature increases. Carrier concentration of grown single crystals are evaluated by the Hall effect. Lattice thermal conductivity of pristine SnSe is 0.61 W mK−1, that decreased by copper doping to 0.44 W mK−1 at 310 K and for both the crystals it shows decrement as temperature increases to 483 K. Seebeck coefficient of the grown SnSe and Cu doped SnSe are positive and obtained values are 536.44 and 492.90 μV K−1 respectively at 310 K that confirm the p‐type semiconducting nature. Power factor, Figure of merit and thermoelectric compatibility factor of grown pristine SnSe is 0.25 × 108 μV mK−2, 0.005 and 0.02 Volt−1 respectively and shows improvement in Cu doped SnSe, i.e., 0.08 × 108 μV mK−2, 0.017 and 0.07 Volt−1 respectively at 310 K. This shows Cu doping in SnSe makes it an effective thermoelectric device contender.

Thermal decomposition study of SnSe single crystals

Enhanced Thermoelectric Properties of SnSe Thin Films Grown by Pulsed Laser Glancing-Angle Deposition

Growth of SnSe Single Crystal Via Vertical Vapor Deposition Method and Characterization of Its Thermoelectric Performance

One-Order Decreased Lattice Thermal Conductivity of SnSe Crystals by the Introduction of Nanometer SnSe2 Secondary Phase

Thermoelectric properties of SnSe and single crystals

Growth of Large Size SnSe Single Crystal and Comparison of Its Thermoelectric Property with Polycrystal

Solvothermal Route to Tin Monoselenide Bulk Single Crystal with Different Morphologies

Multiple Emerging Nano-Phases Are at the Origin of the Low Lattice Thermal Conductivity of SnSe?

In-situ Micro-Raman Study of SnSe Single Crystals under Atmosphere: Effect of Laser Power and Temperature.

Influence of pressure on phase transition, electronic and thermoelectric properties of SnSe

Investigation of the Electronic Structure and Lattice Dynamics of the Thermoelectric Material Na-doped SnSe

Evidence for hard and soft substructures in thermoelectric SnSe

Broadband (NIR-Vis-UV) photoresponse of annealed SnSe films and effective oxidation passivation using Si protective layer

Charge Transport in Thermoelectric SnSe Single Crystals

Copper Intercalation Effect on Thermoelectric Performance of Pristine Tin Selenide

Insight into the intrinsic microstructures of polycrystalline SnSe based compounds

Phonon Spectra and Lattice Thermal Conductivity of High-Performance Thermoelectric SnSe

Microstructural Instability and Its Effects on Thermoelectric Properties of SnSe and Na-Doped SnSe

Thermoelectric transport properties of pristine and Na-doped SnSe1-xTex polycrystals.

Tin Selenide (SnSe): Growth, Properties, and Applications

Synthesis Of Snse In Various Alkaline Media Under Mild Conditions