Abstract:Alloying of corrosion-resistant austenitic steels with nitrogen is widely used in production to stabilize austenite and to improve the strength and other properties of the metal. The possibility of alloying titanium-containing steels with nitrogen by introducing nitrogen into the melt is not possible, as it causes formation of the coarse defects in steel during casting and solidification of the metal (twisting of the peel, large nitride inclusions, accumulations of nitrides, etc.). The method of high-temperature gas nitriding can be alternative to liquid-phase nitriding for alloying austenitic titanium-containing chromium-nickel steels with nitrogen in order to increase their strength properties. In this work, we investigated the possibility of increasing the strength characteristics of thin-sheet austenitic corrosion-resistant Cr – Ni – Ti (Kh18N12T type) steel, containing 1.5 % and 3 % of titanium, through the use of solid-phase high-temperature nitriding. The nitriding was carried out at a temperature of 1000 – 1100 °С in an atmosphere of pure nitrogen for 5 or 8 hours. The average mass fraction of nitrogen in the samples after nitriding for 5 hours was 0.6 % and 0.7 % for the steels with 1.5 and 3 % of titanium, respectively, and after nitriding for 8 hours – 0.8 % and 0.9 %. It was shown that high-temperature nitriding followed by annealing provides a significant (by 2 – 3 times) increase in the metal strength characteristics compared with the state before nitriding, but reduces the ductility. Ductility of the steel is restored during final processing. For Kh18N12Т type steel with 1.5 % of titanium, an increase in the yield strength is obtained – by 3.3 times (from 180 to 600 MPa), strength – by 1.8 times (from 540 to 970 MPa), with a relative elongation of 28 %. An additional increase in strength properties was not found for the steel with 3 % titanium. The obtained results show the possibility of obtaining thin-sheet titanium-containing high-nitrogen steel (or products from it, for example, thin-walled pipes) by applying solid-phase high-temperature nitriding.

Mechanism of ion nitriding of 316L austenitic steel by active screen method in a hydrogen-nitrogen atmosphere

Effects of Plasma-Chemical Composition on AISI 316L Surface Modification by Active Screen Nitrocarburizing Using Gaseous and Solid Carbon Precursors

Functional properties of expanded austenite generated on AISI 316L by plasma nitrocarburizing using different active screen materials

Kinetics of Iron Nitride Layer Growth during the Nitriding of AISI 1085 Non-Alloy Steel and AISI 52100 Alloy Steel

The Effectiveness of Active Screen Method in Ion Nitriding Grade 5 Titanium Alloy

Active screen plasma nitriding of 2Cr13 martensitic stainless steel

Characteristics of the Nitrided Layer Formed on AISI 304 Austenitic Stainless Steel by High Temperature Nitriding Assisted Hollow Cathode Discharge

Microstructure and Corrosion Resistance of Nitrogen-Rich Surface Layers on AISI 304 Stainless Steel by Rapid Nitriding in a Hollow Cathode Discharge

Enhancement of Pitting Corrosion Resistance of Austenitic Stainless Steel Through Deposition of Amorphous/Nanocrystalline Oxy-nitrided Phases by Active Screen Plasma Treatment

Wear and Corrosion Properties of AISI 420 Martensitic Stainless Steel Treated by Active Screen Plasma Nitriding

Effect of electric potentials on high-temperature plasma nitriding of 2Cr13 stainless steel with active screen assistedEinfluss des elektrischen Potenzials auf Hochtemperatur-Plasmanitrieren von rostfreiem Stahl (2Cr13)

Improved Mechanical Properties, Wear and Corrosion Resistance of 316L Steel by Homogeneous Chromium Nitride Layer Synthesis Using Plasma Nitriding

Mechanical and Microstructural Characterization of AISI 316L Stainless Steel Superficially Modified by Solid Nitriding Technique

Effect of electric potentials on high‐temperature plasma nitriding of 2Cr13 stainless steel with active screen assisted

Effect of Machine Pin-Manufacturing Process Parameters by Plasma Nitriding on Microstructure and Hardness of Working Surfaces

STRUCTURE AND MECHANICAL PROPERTIES OF AUSTENITIC Cr – Ni – Ti STEELS AFTER HIGH-TEMPERATURE NITRIDING

Nitriding behavior and corrosion properties of AISI 304L and 316L austenitic stainless steel with deformation-induced martensite

Low-Temperature Plasma Nitriding for Austenitic Stainless Steel Layers with Various Nickel Contents Fabricated via Direct Laser Metal Deposition

Structure and corrosion behavior of ultra-thick nitrided layer produced by plasma nitriding of austenitic stainless steel

Corrosion and Micro-Abrasion Properties of an AISI 316L Austenitic Stainless Steel after Low-Temperature Plasma Nitriding

Increasing the Wear Resistance of Structural Steel Parts by Ion Nitriding during Complex Surface Preparation Using the Dry Electropolishing Method