Abstract:It is an urgent desire to decrease release of methane, a potential greenhouse gas, over methane-oxidation catalysts. However, the commonly used Pd-based catalysts normally suffer from poor hydrothermal stability. Here, we report a Pd-Pt bimetallic nano-catalyst stabilized by magnesia-alumina spinel via a facile doping strategy for lean methane combustion. The promoted effects of platinum on the hydrothermal stability of the catalyst are confirmed by XRD, HRTEM, STEM, XPS, CO-DRIFTS characterizations. Pd-Pt bimetallic catalyst can almost maintain its intrinsic catalytic activity (2.7 × 10−5 molCH4 gnoble metal-1s-1 at 260 °C) after harshly hydrothermal aging, while the aged analogous sample without Pt promotion presents remarkably reduced catalytic performance with an increment in CH4 light-off temperature of ca. 50 °C. Kinetic analysis further reveals a much higher turnover frequency (0.011 s-1 at 260 °C) and lower apparent activation energy (119 kJ/mol) of CH4 oxidation on the aged Pd-Pt bimetallic samples. Pt stabilized by magnesia-alumina spinel has a strong interaction with PdO. This interaction could stabilize Pd species in active PdO and also suppress the decomposition of active PdO to less reactive Pd°. Consequently, the sintering resistance of Pt and PdO crystallite and the electron interaction between them could be responsible for the enhanced hydrothermal stability.

Insights into the role of Pt on Pd catalyst stabilized by magnesia-alumina spinel on gama-alumina for lean methane combustion: Enhancement of hydrothermal stability