UV-light-induced photocatalytic performance of reusable MnFe-LDO–biochar for tetracycline removal in water

Khawla Abdulmutalib Azalok,Akeem Adeyemi Oladipo,Mustafa Gazi

DOI: https://doi.org/10.1016/j.jphotochem.2020.112976

2021-01-01

Abstract:<p>A high-efficiency layered double oxide-biochar hybrid (MnFe-LDO–biochar) catalyst was successfully synthesized by the co-precipitation-calcination process and used to effectively remove tetracycline (TC) pollution. The characterization results verified that MnFe-LDO–biochar possesses a specific surface area of 524.8 m² g⁻¹, appropriate bandgap (2.85 eV), a high photocurrent response (3.8 µA cm^–2), a saturation magnetization of 28.5 emu g⁻¹ and a mixture of interconnected pores. 40% of TC was removed after 30 min when 50 mL TC solution (20 mg L⁻¹) was treated with 50 mg MnFe-LDO–biochar in the dark and reached ∼98% degradation rate within 240 min upon exposure to a UV light. Notably, in the presence of H₂O₂ or K₂S₂O₈, the degradation rate of MnFe-LDO–biochar was shortened to 60 min with an average pseudo-first-order rate constant of 0.0445 min⁻¹. The antibiotic removal rate of the cost-competitive MnFe-LDO–biochar surpassed several reported materials and maintained ∼80% reuse efficiency after 3^rd successive cycles. The TC photodegradation mechanism is multiprocess induced majorly by ^•OH and ^•SO₄⁻ while <em>h⁺</em> and ^•O₂⁻ contributed partly to the mineralization. This work highlights the powerful synergistic combination of layered double oxide (LDO) and biochar.</p>