Abstract:Purpose This paper aims to design the nano-titanium dioxide (TiO 2 ) coating system which has superhydrophilic property, self-cleaning mechanism and antifog property as well as strong adhesion on glass substrate. Design/methodology/approach Two hydrophilic materials have been used such as TiO 2 nanoparticles as fillers and hydrophilic copolymer, Pluronic F-127 by using simple sol–gel approach. The prepared solution was applied onto glass through dip- and spray-coating techniques and then left for drying at ambient temperature. Findings The nano-TiO 2 superhydrophilic coating has achieved the water contact angle of 4.9° ± 0.5°. The superhydrophilic coating showed great self-cleaning effect against concentrated syrup and methylene blue where thin layer of water washes the dirt contaminants away. The nano-TiO 2 coating exhibits great antifog performance that maintains high transparency of around 89% when the coated glass is placed above hot-fog vapor for 10 min. The fog droplets were condensed into water film which allowed the transmission of light through the glass. The strong adhesion of coated glass shows no total failure at scratch profile when impacted with scratch load of 500, 800 and 1,200 mN. Research limitations/implications Findings will be useful in the development of self-cleaning superhydrophilic coating that is applicable on building glass and photovoltaic panel. Practical implications The developed nano-TiO 2 coating is developed by the combination of hydrophilic organic copolymer–inorganic TiO 2 network to achieve great superhydrophilic property, optimum self-cleaning ability and supreme antifog performance. Social implications The findings will be useful for residents in building glass window where the application will reduce dust accumulation and keep the glass clean for longer period. Originality/value The synthesis of nano-TiO 2 superhydrophilic coating which can be sprayed on large glass panel and cured at ambient temperature.

Preparation of PTFE-coated SiO2 nanorod films for self-cleaning application

Super-hydrophobic and Self-cleaning PVDF Film Fabricated by Chemical Bath Deposition

Study on Nano- Titanium Dioxide Thin Film Coated on Self-cleaning Glass Surface

Fabrication of Self-Cleaning Polyvinylidene Fluoride Film

Durable self-cleaning nano-titanium dioxide superhydrophilic coating with anti-fog property

Preparation and Characterization of PVDF Film with Self-cleaning Property

Fabrication of TiO2 ̶ KH550 ̶ PEG Super-Hydrophilic Coating on Glass Surface without UV/Plasma Treatment for Self-Cleaning and Anti-Fogging Applications

Fabrication of transparent silica-silica nanotube/PFTS nano-composite thin films with superhydrophobic, oleophobic, self-cleaning and anti-icing properties

Highly Transparent and Highly Hydrophobic Coating for Outdoor Camera Window Glass: Fabrication, Transparency, and Hydrophobicity

Preparation of high transparent hydrophobic glass surface and its self-cleaning property

Superhydrophilic Smart Coating for Self-Cleaning Application on Glass Substrate

Self‐cleaning antireflected surfaces based on treated PEO/SiO2 nanocomposite films

Preparation of TiO2:PMMA:PVA nanocomposite thin film as a smart coating as the self-cleaning application

Preparation of transparent and robust superhydrophobic surfaces for self-cleaning applications

Durable Broadband and Omnidirectional Ultra-antireflective Surfaces

Preparation of Anti-Reflection Glass Surface with Self-Cleaning and Anti-Dust by Ammonium Hydroxide Hydrothermal Method

Development of self-cleaning polydimethylsiloxane/nano-calcium carbonate-titanium dioxide coating with fog-resistance response for building glass

Enhancing glass surface hydrophobicity: the role of Perfluorooctyltriethoxysilane in advanced surface modification

A nanotubular coating with both high transparency and healable superhydrophobic self-cleaning properties

The Preparation and Characterization of Uniform Nanoporous Structure on Glass

Spin‐coated transparent hydrophobic, self‐cleaning surfaces using PDMS, iTES with PF‐127