Abstract:Producing active thin films coated on supports resolves many issues of powder-based photo catalysis and energy harvesting. In this study, thin films of C-N-TiO2 were prepared by dynamic spin coating of C-N-TiO2 sol-gel on glass support. The effect of spin speed and sol gel precursor to solvent volume ratio on the film thickness was investigated. The C-N-TiO2-coated glass was annealed at 350 °C at a ramping rate of 10 °C/min with a holding time of 2 hours under a continuous flow of dry N2. The C-N-TiO2 films were characterised by profilometry analysis, light microscopy (LM), and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The outcomes of this study proved that a spin coating technique followed by an annealing process to stabilise the layer could be used for immobilisation of the photo catalyst on glass. The exposure of C-N-TiO2 films to UV radiation induced photocatalytic decolouration of orange II (O.II) dye. The prepared C-N-TiO2 films showed a reasonable power conversion efficiency average (PCE of 9%) with respect to the reference device (15%). The study offers a feasible route for the engineering of C-N-TiO2 films applicable to wastewater remediation processes and energy harvesting in solar cell technologies.

Spin Coating Immobilisation of C-N-TiO2 Co-Doped Nano Catalyst on Glass and Application for Photocatalysis or as Electron Transporting Layer for Perovskite Solar Cells