Abstract:The cycle life and coulomb efficiency of silicon anode materials for lithium-ion batteries are greatly reduced due to the large volume change during charge-discharge process, which limits its commercial application. Herein, a silicon/N-rich carbon anode material was prepared by using N-rich gelatin as the raw material. Two different processing methods, hot-drying and freeze-drying, were adopted to prepare Si/C composite-based electrodes, (Si@GC-H and Si@GC-F). Compared with the traditional hot-drying method to prepare the Si@GC-H composite, the Si@GC-F composite showed good electrochemical performance by controlling the dispersibility of Si nanoparticles using hydrogel and gas gel. The Si@GC-F composite exhibited an even distribution of Si nanoparticles in the carbonaceous matrix, which prevented the agglomeration of Si nanoparticles. The specific discharge capacity of Si@GC-F composite (Si content is only 20.06%) was 528.1 mAh g–1after 100 cycles at the current density of 0.1 A g−1, and the Coulombic efficiency was 99.7%. The specific capacity can fully meet the existing commercial cathode electrode matching.

Comparing the Electrochemical Performance of Silicon/N-Rich Carbon Composite-based Anode Material Prepared by Hot- drying and Freeze-drying methods