Abstract:Metal and nitrogen-doped carbon (M-N-C) catalysts are generally considered to be ideal substitutes for platinum-based noble metal oxygen reduction catalysts. Owing to the significant Fenton effect of the Fe element and the subsequent instability, the Fenton-free Co-based N-C catalyst should perform better in ORR. Pyrolysis of metal-organic frameworks (MOFs) is commonly used to make Co-based N-C catalysts. Still, most of the MOF-derived catalysts reported so far have a microporous structure, which results in hindered mass transfer and partial Co-N-x active sites that cannot function as catalysis. Herein, Co nanoclusters (NCs) with high loading (7.96 wt%) were prepared on hierarchically porous carbon substrates via a carboxylate-assisted strategy. The mesoporous structure of Co nanoclusters/nitrogen-doped hierarchically porous carbon (Co NCs/HPNC) can facilitate mass transport. The smaller size Co nanoclusters can increase the contact area between the carbon matrix and Co-N-x active sites to effectively expose more active centers and increase the density of Co-N-x active sites. A synergistic effect of the two can greatly improve ORR results. Surprisingly, the Co NCs/HPNC catalyst shows excellent ORR activity under alkaline conditions, and Co NCs/HPNC has a better half-wave potential (0.88 V vs. 0.84 V) compared with 20 wt% Pt/C. And it only loses 5% of its current density after 36,000 s of operation, which is significantly less than Pt/C (20%). Furthermore, Co NCs/HPNC battery have a greater open-circuit potential, power density, and specific capacity than Pt/C-based zinc-air batteries (1.51 V, 109.6 mW cm(-2), 818.1 mAh gZn(-1) vs. 1.46 V, 92.4 mW cm(-2), 716.8 mAh gZn(-1)). This discovery paves the way for high-efficiency electrocatalysts with hierarchically porous architectures and a large number of metal loads to be developed. (C) 2022 Elsevier B.V. All rights reserved.

ZIF-derived zinc decorated cobalt nanoparticles for efficient oxygen reduction and Zn-air batteries

Experimental and theoretical insights into cobalt nanoparticles encapsulated in N- and S-codoped carbon as advanced bifunctional electrocatalyst for rechargeable zinc-air batteries

Co single atoms and nanoparticles dispersed on N-doped carbon nanotube as high-performance catalysts for Zn-air batteries

Understanding the Synergistic Effects of Cobalt Single Atoms and Small Nanoparticles: Enhancing Oxygen Reduction Reaction Catalytic Activity and Stability for Zinc‐Air Batteries

Co3Fe7/CoCx nanoparticles encapsulated in nitrogen-doped carbon nanotubes synergistically promote the oxygen reduction reaction in Zn-air batteries

Carboxylate-assisted ZIF-derived Co nanoclusters anchoring hierarchically porous carbon as high-efficient zinc-air batteries cathode catalysts

ZIF ‐mediated anchoring of Co species on N‐doped carbon nanorods as an efficient cathode catalyst for Zn‐air batteries

Zeolitic Imidazole Framework Derived N-doped Porous Carbon/metal Cobalt Nanoparticles Hybrid for Oxygen Electrocatalysis and Rechargeable Zn–air Batteries

Carbon dots-derived carbon nanoflowers decorated with cobalt single atoms and nanoparticles as efficient electrocatalysts for oxygen reduction

Co Nanoislands Rooted on Co-N-C Nanosheets As Efficient Oxygen Electrocatalyst for Zn-Air Batteries.

Nitrogen-doped Porous Carbon Encapsulates Multivalent Cobalt-Nickel As Oxygen Reduction Reaction Catalyst for Zinc-Air Battery

ZIF-8-assisted pyrolysis to synthesize cobalt-modified nitrogen‐sulfur co-doped carbon nanofibers for zinc-air batteries

Dispersed Cobalt Nanoparticles in the Nitrogen Doped Carbon Black As Efficient Catalysts for Oxygen Reduction Reaction and Zinc-Air Batteries

Cubic imidazolate frameworks-derived CoFe alloy nanoparticles-embedded N-doped graphitic carbon for discharging reaction of Zn-air battery

Trimetallic Zeolitic imidazolite framework-derived Co nanoparticles@CoFe-nitrogen-doped porous carbon as bifunctional electrocatalysts for Zn-air battery

In Situ, Fast Constructing Interface/doping-Engineered NiCo Bimetal-Based Composites Boosting Electrocatalytic Oxygen Reduction for Zinc-Air Battery

Preparation of CoN Co-Doped Carbon Nanosheets Electrocatalyst for Efficient Oxygen Reduction Reaction in Zinc-Air Battery

Nitrogen-doped Carbon Nanotube Encapsulating Cobalt Nanoparticles Towards Efficient Oxygen Reduction for Zinc–air Battery

Cobalt Nanoparticles Encapsulated in Iron and Nitrogen Co-Doped Urchin-Like Porous Carbons As an Efficient Bifunctional Oxygen Reversible Catalyst for Zn-air Batteries

Cobalt Nanoparticles Encapsulated in Nitrogen-Doped Carbon Nanotube as Bifunctional-Catalyst for Rechargeable Zn-Air Batteries

Cobalt and Nitrogen Co-Doping of Porous Carbon Nanosphere As Highly Effective Catalysts for Oxygen Reduction Reaction and Zn-air Battery