Effect of Zn content on the dynamic softening of Al–Zn–Mg–Cu alloys during hot compression deformation

Jie Tang,Jinhai Wang,Jie Teng,Guan Wang,Dingfa Fu,Hui Zhang,Fulin Jiang

DOI: https://doi.org/10.1016/j.vacuum.2020.109941

IF: 4

2021-02-01

Vacuum

Abstract:Increasing Zn content in Al–Zn–Mg–Cu alloys can improve the strength but reduce the ductility. Hot deformation is usually employed to process ultra-high strength Al–Zn–Mg–Cu alloys with high Zn addition to address the limitation of low workability. In the present work, uniaxial hot compression tests have been performed on Al–Zn–Mg–Cu alloys with different Zn contents at deformation temperatures of 300 °C and 400 °C, and strain rates of 0.01 s−1 and 0.1 s−1 respectively to study the influence of Zn content on dynamic softening. The results showed that with the increase of Zn content, the work hardening rate of Al–Zn–Mg–Cu alloys during the early stage of deformation was accelerated. And the peak stress and hot deformation activation energy increased first and then decreased slightly. Under deformation condition with high Z value, the dynamic softening of Al–Zn–Mg–Cu alloys increased gradually because that the increased Zn content accelerated the process of dynamic precipitation which was mainly responsible for the dynamic softening. While at low Z value, dynamic softening decreased with increasing Zn content when dynamic recovery and dynamic recrystallization were the predominant softening mechanisms. The addition of Zn inhibited the progress of dynamic recovery and dynamic recrystallization resulting and then decelerated dynamic softening.

materials science, multidisciplinary,physics, applied