Surface-modified graphite felt incorporating synergistic effects of TiO 2 decoration, nitrogen doping, and porous structure for high-performance vanadium redox flow batteries
Yu-Sheng Hsiao,Jen-Hsien Huang,Hong-Yu Lin,Wei Kong Pang,Min-Tzu Hung,Ta-Hung Cheng,Shih-Chieh Hsu,Huei Chu Weng,Yu-Ching Huang
DOI: https://doi.org/10.1016/j.surfcoat.2024.130785
IF: 4.865
2024-04-17
Surface and Coatings Technology
Abstract:Construction of porous surface, decoration of metal oxide, and introduction of defects are three major strategies to improve the electrocatalytic capability of graphite felt (GF) for vanadium redox flow battery (VRFB). In this study, we have successfully achieved the urea-assisted deposition of TiO 2 onto GF, resulting in a synergistic effect that realizes the three modifications mentioned above, through a facile one-pot approach. During the post-annealing process, the decorated TiO 2 can further undergo carbon-thermal reduction to etch the GF surface, leading to a porous surface. Additionally, the defective structures such as oxygen defects and nitrogen doping also be can simultaneously incorporated in the modified GF. As a result, the modified GF shows a dramatically improved electrocatalytic capability towards the VO 2+ /VO 2 + redox reactions due to better hydrophilicity, larger surface area, and numerous oxygen defects. The VRFB with the modified GF electrode can deliver the coulombic efficiency (CE), voltage efficiency (VE), and energy efficiency (EE) of 95.0, 81.8, and 77.8 %, respectively, at 160 mA/cm 2 , which are much better than those of VRFB based on untreated GF.
physics, applied,materials science, coatings & films