Synergistic role of electron-trapped oxygen vacancy and exposed TiO2 [0 0 1] facets toward electrochemical p-nitrophenol reduction: Characterization, performance and mechanism

Congcong Ni,Yifan Li,Xianzhe Meng,Shuliang Liu,Siyi Luo,Jing Guan,Bo Jiang

DOI: https://doi.org/10.1016/j.cej.2021.128485

IF: 15.1

2021-05-01

Chemical Engineering Journal

Abstract:<p>Despite the fact that electron-trapped oxygen vacancy and [0 0 1] facets fundamentally affect the reactivity of TiO₂, their synergistic role in the electrochemical activity of TiO₂ toward p-nitrophenol (p-NP) reduction is still unknown. In this study, defective and [0 0 1] facets engineered TiO₂ cathode, i.e. Ti/TiO_2−x-0 0 1, was prepared for p-NP reduction. In comparison to defective Ti/TiO₂ cathode with [1 0 1] facets (Ti/TiO_2−x-1 0 1), the combination of the electron-trapped oxygen vacancy and [0 0 1] facets exhibited a synergistic effect to improve the electrochemical reduction efficiency of TiO₂. Density functional theory calculations verified that the introduction of [0 0 1] facets and electron-trapped oxygen vacancy on TiO₂ was beneficial to facilitate electron transfer and improve the indirect reduction efficiency for p-NP electrochemical reduction. Moreover, the electron-trapped oxygen vacancy extent of Ti/TiO_2−x-0 0 1 was modulated by adjusting reduction temperature (250–650 °C). The maximum electron-trapped oxygen vacancy amount of Ti/TiO_2−x-0 0 1 was attained at the reduction temperature of 350 °C, which resulted in the highest p-NP reduction efficiency of 99.3%, accompanying the p-AP selectivity of 89.5%. In this case, the abundant active and adsorption sites were provided on the surface of Ti/TiO_2−x-0 0 1 prepared at 350 °C, in which p-NP adsorption coefficient and electrochemical surface area increased to 1.01 L mg⁻¹ and 25 cm², respectively. Generally, this work provides a paradigm for the design of efficient non-metallic catalyst for nitroaromatic chemicals reduction.</p>

engineering, chemical, environmental