Electrocatalytic Oxidation of Formic Acid Using Au @ Pt Dendrimer-Encapsulated Nanoparticles
I. Ravikumar,Liang Zhang,Graeme Henkelman,Richard M. Crooks
DOI: https://doi.org/10.1021/ja4010305
IF: 15
2013-01-01
Journal of the American Chemical Society
Abstract:We report electrocatalytic oxidation of formic acid using monometallic and bimetallic dendrimer-encapsulated nanoparticles (DENs). The results indicate that the Au147@Pt DENs exhibit better electrocatalytic activity and low CO formation. Theoretical calculations attribute the observed activity to the deformation of nanoparticle structure, slow dehydration of formic acid, and weak binding of CO on Au147@Pt surface. Subsequent experiments confirmed the theoretical predictions. I this Communication we show that electrochemically synthesized nanoparticles consisting of a 147-atom Au core and a Pt shell (Au147@Pt) facilitate the direct oxidation of formic acid to carbon dioxide. Specifically, experiments and first-principles calculations show that ∼2-nm-diameter Au147@ Pt dendrimer-encapsulated nanoparticles (DENs) undergo a structural distortion that suppresses formation of adsorbed CO (COads) compared to Pt-only DENs. 2 This finding is significant, because it represents an unusual case in which a well-defined structural deformation of a very small nanoparticle results in a dramatic improvement in catalytic performance. Formic acid is used as a substitute fuel for hydrogen in proton exchange membrane fuel cells (PEMFCs), because oxidation of hydrogen and formic acid occurs at similar thermodynamic potentials. Electro-oxidation of HCOOH to CO2 on Pt electrocatalysts occurs via two mechanisms: (1) through formation of a reactive intermediate (direct oxidation pathway), and (2) through formation of COads and subsequent oxidation of COads to CO2 (indirect oxidation pathway). 4 The second pathway is problematic, because COads poisons the Pt surface. However, it has been shown that the presence of Au can improve the CO tolerance of Pt, and hence its catalytic performance. For example, Xu and co-workers found that Au@Pt nanoparticles having submonolayer Pt shells exhibit improved electrocatalytic activity for formic acid oxidation due to specifically engineered electronic interactions between the two metals. An alternative to improving CO tolerance is to simply avoid CO altogether. For example, Masel and coworkers found that carbon-supported Pd is highly active for formic acid oxidation, because it favors the direct oxidation pathway. However, Pd/C suffers significant loss in activity during formic acid oxidation due to slow adsorption of CO-like intermediates, bridge-bonded formate, perchlorate, and other anions. The DENs in this study were synthesized, and their structure characterized, using methods we previously reported. Briefly, Pt147 DENs were synthesized by adding 147 equiv of K2PtCl4 to a 2.0 μM aqueous solution of a sixth-generation, hydroxyl-terminated poly(amidoamine) dendrimer (G6-OH). The Pt was allowed to complex with the dendrimer for 3 days, and then a 10-fold excess of NaBH4 was added to reduce the G6-OH(Pt)147 precursor to G6-OH(Pt147) DENs. A similar procedure was used for the synthesis of Au147 DENs, except the reduction was initiated almost immediately after addition of HAuCl4 to avoid competitive reduction by the hydroxyl groups of the dendrimers. Pt and Au DEN-modified electrodes were prepared by sonicating an aqueous solution, containing 20% isopropyl alcohol, with 2 mg mL−1 of Vulcan EC-72R carbon for 5 min, and then drop-casting 4.0 μL of the resulting ink onto a freshly polished glassy carbon electrode (GCE). The electrode was then dried at room temperature. Following a method pioneered by Adzic and co-workers, and our previous experimental procedure, Au147@Pt DENs were synthesized by electrochemical underpotential deposition (UPD) of Pb onto Au147 DENs, followed by galvanic exchange with PtCl4 2−. Specifically, Au147 DENs were immobilized on a GCE, and then a monolayer of Pb was added to the Au core by UPD from a N2-saturated aqueous solution containing 1.0 mM Pb(NO3)2 and 0.10 M HClO4. Next, 10.0 mL of a 1.0 mM K2PtCl4 solution was added to initiate galvanic exchange of Pb for Pt. The resulting DENs were then characterized by UV−vis spectroscopy, transmission electron microscopy, and electrochemical methods (Supporting Information) and found to be consistent with our previous findings. Figure 1 shows cyclic voltammograms (CVs) for formic acid oxidation using Au147, Pt147, and Au147@Pt DEN-modified GCEs in 0.10 M HClO4 containing 0.10 M HCOOH. The Au147 DENs do not exhibit detectable activity for formic acid oxidation. In contrast, the Pt147 DEN-modified electrode reveals two peaks at −0.12 and 0.21 V (vs Hg/Hg2SO4) in the scan toward more positive potentials. These are attributable to the direct oxidation of HCOOH to CO2 and oxidation of COads, generated by dehydration of HCOOH, respectively. The low ratio (2.8) of the current densities (jp /jp , Table 1) for these two peaks indicates a substantial degree of indirect electrocatalytic oxidation of formic acid on Pt147 DENs. 16 Upon scan reversal, a single peak is observed at −0.24 V, which corresponds to direct oxidation of HCOOH to CO2. With Received: January 29, 2013 Published: April 8, 2013 Communication