Abstract:Pure copper is very soft, however, hardening the pure copper with most strengthening mechanisms leads to a significant reduction in electrical conductivity. Grain refinement is a better strengthening mechanism to maintain high enough electrical conductivity. Plastic deformation at room temperature followed by post-annealing is one of the best methods to achieve fine-grained metals and alloys. In this research, the high-temperature annealing behavior of cold-rolled electrolytic tough-pitch (ETP) copper sheets was studied. 90 % asymmetric cold rolling followed by high-temperature post-annealing at 673 K for 1, 2, 5, 10, 30, 60, and 120 min were applied on the copper. The microstructure was significantly changed with increasing annealing time from 1 to 2 min owing to full recrystallization. With increasing the annealing duration, the grain size is increased. The formation of equiaxed grains with a smaller size (∼9 μm) compared to the full-annealed (initial) sample (∼68 μm) is observed after the longest time of post-annealing (120 min) due to the pinning effect of Cu2O particles. The post-annealed copper sheets processed by asymmetric rolling (in this work) exhibited a more homogeneous microstructure through the thickness compared to the symmetric rolling due to more uniform stored strain energy. The results showed that the first deformed grains that undergo recrystallization during post-annealing are Goss-oriented grains. With an increase in the post-annealing time, the S and Copper components were eliminated and a strong Cube and P texture orientations were formed. Interestingly, after 1 min of post-annealing, the yield and tensile strength enhanced to 410.2 MPa and 418.6 MPa owing to the annealing hardening phenomenon. The hardness and strength reached a constant value after the post-annealing for 10 min and above. With increasing the post-annealing duration, the central area of fracture surfaces (consisting of ductile dimples) became larger and the outer region (consisting of flat surfaces and shear dimples) became smaller, showing a shift towards perfect ductile fracture. With the increase of post-annealing time from 1 min to 120 min, the electrical conductivity was increased from 77.6 to 97.5 %IACS. The presence of the Cube texture increased the electron mobility compared to the P orientation, by reducing the mean distance that they can travel without scatter. From the obtained results, it can be concluded that the asymmetric cold rolling followed by high-temperature post-annealing is capable of strength improvement and maintaining electrical conductivity in copper.

The Evolution of Microstructure and Resistance in Electroplated Copper Films by Linear Integrated Laser Scanning Annealing

Al-clad Cu Bond Wires for Power Electronics Packaging: Microstructure Evolution, Mechanical Performance, and Molecular Dynamics Simulation of Diffusion Behaviors

Experiment Study of Laser Thermal Enhanced Electrochemical Deposition

Effect of in-line electron beam treatment on the electrical performance of Cu/organic low-k damascene interconnects

Microstructure evolution in Cu-2.13Fe-0.026P (wt%): The contribution of texture intensity to residual stress variation

Research on Effect of Annealing on Copper Deposited by Electroplating in High Density TSV

The kinetics and mechanism of room-temperature microstructural evolution in electroplated copper foils

The Influence of Heat Treatment on Microstructure and Properties of Selective Laser Melting CuCrZr Alloy

Failure Mode Analysis in Microsecond UV Laser Annealing of Cu Thin Films

Tailoring surface properties and corrosion resistance of laser shock peened Ti6Al4V alloy by low-temperature annealing

Electropulsing-enhanced atomic diffusion and recrystallization to optimize mechanical properties of Al/Cu laminated metal composites

The effect of annealing on trapped copper oxides in particle-particle interfaces of cold-sprayed Cu coatings

Effect of annealing temperature on microstructure and tensile properties of copper/aluminum composite thin strip

Enhanced adhesion strength between electroplated Cu and ABF substrate with isothermal annealing treatment

Room-Temperature Microstructural Evolution of Electroplated Cu Studied by Focused Ion Beam and Positron Annihilation Lifetime Spectroscopy

Anisotropic material properties of pure copper with fine-grained microstructure fabricated by laser powder bed fusion process

The Portevin-Le Chatelier (PLC) effect in an Al-Cu aluminum alloy fabricated by selective laser melting

High-temperature annealing behavior of cold-rolled electrolytic tough-pitch copper

Effect of Annealing Process on the Properties of Through-Silicon-via Electroplating Copper

Influence of annealing conditions on the mechanical and microstructural behavior of electroplated Cu-TSV

Effect of low temperature annealing on microstructure and properties of copper foil