Abstract:Cross-linked polyethylene (XLPE) has been widely used as insulation material for cables. In 2019, the highest voltage level AC 500 kV XLPE submarine cable has been operated in Zhoushan, China. The irreversible degradation poses a safety hazard to the operation of submarine cable. Therefore, it is necessary to investigate the physical, chemical and electrical properties of XLPE submarine cable insulation under aging condition and explore the method for its deterioration degree assessment. In this paper, the AC 500 kV XLPE submarine cable insulation material was thermally aged at 130 °C. The deterioration characteristics of materials were analyzed based on morphology, chemical structure, mechanical property, thermal property and dielectric properties. Multiple characteristic parameters were extracted and new deterioration condition assessment model was established. Results show that the physicochemical characteristic parameters including retention rate of elongation at break, carbonyl index (CI) based on FTIR, full-width at half-maximum (FWHM) of the diffraction peak based on XRD, melting enthalpy based on DSC analysis, and the dielectric characteristic parameters including modified Cole-Cole model parameter $chi _{mathrm {salpha }}$ and AC breakdown strength are sensitive to deterioration condition of XLPE material. According to the change of elongation retention at break, the deterioration condition of XLPE sample was divided into enhanced stage, wear-out stage and disposal stage. The new multi-factor deterioration condition assessment model including six characteristic parameters (retention rate of elongation at break, CI, FWHM, melting enthalpy, modified Cole-Cole model parameter $chi _{mathrm {salpha }}$ , AC breakdown strength) was successfully established by g-ey correlation analysis. The new model can reflect the property of mechanical, chemical, thermal and dielectric property and has prominent effect in differentiating deterioration degree of the AC 500 kV XLPE submarine cable insulation material.

Understanding of Pulse Voltage Response Analysis for Degradation in XLPE Cable Using Equivalent Circuit Model

Investigation on Thermal Aging and Degradation of XLPE for High Voltage Cable Applications

Propagation and Partial Discharge Characteristics of Electrical Trees in 110 Kv XLPE Cable Insulation at Power Frequency Applied Voltage

Partial Discharge and Growth Characteristics of Electrical Trees in 110kV XLPE Cable Insulation at High Temperature

Studies of the Polarization/depolarization Current Characteristics of XLPE Cable

Analysis of XLPE Cable Health Assessment Parameters under Various Test Voltages by PDC Method

Investigation of partial discharge characteristics in XLPE cable insulation under increasing electrical stress

Fast Detection Method on Water Tree Aging of MV Cable Based on Nonsinusoidal Response Measurement

Polarization-depolarization Current Method for XLPE Cable Insulation Diagnosis

Evaluation of Voltage Endurance Characteristics for New and Aged XLPE Cable Insulation by Electrical Treeing Test

Research on the Carrier Characteristics of Power Cables Considering the Aging Status of Insulation and Semiconducting Layers

Study on Partial Discharge Pulse Attenuation Characteristics in 110 Kv Xlpe Power Cable

Evaluation Analysis of 10 kV XLPE Cable's Operation Condition

Space Charge and Conduction Characteristics of XLPE with Different Ageing

Dynamics Model for Electrical Tree Propagation in Cross-Linked Polyethylene Cable Insulation under High Frequency Voltage

The Relationship Between Partial Discharge Behavior and the Degradation of 10 Kv Xlpe Cable Joints

Dielectric loss and partial discharge test analysis of 10 kV XLPE cable

Morphological, Structural, and Dielectric Properties of Thermally Aged AC 500 kV XLPE Submarine Cable Insulation Material and Its Deterioration Condition Assessment

Response and Mechanisms of Water Trees in XLPE Cable Insulation under Superposition Voltage

Physicochemical Origin of Space Charge Dynamics for Aged Xlpe Cable Insulation