Abstract:Syngas conversion is a key platform for efficient utilization of various carbon-containing resources including coal, natural gas, biomass, organic wastes, and even CO2. One of the most classic routes for syngas conversion is Fischer-Tropsch synthesis (FTS), which is already available for commercial application. However, it still remains a grand challenge to tune the product distribution from paraffins to value-added chemicals such as olefins and higher alcohols. Breaking the selectivity limitation of the Anderson-Schulz-Flory (ASF) distribution has been one of the hottest topics in syngas chemistry.Metallic Co0 is a well-known active phase for Co-catalyzed FTS, and the products are dominated by paraffins with a small amount of chemicals (i.e., olefins or alcohols). Specifically, a cobalt carbide (Co2C) phase is typically viewed as an undesirable compound that could lead to deactivation with low activity and high methane selectivity. Although iron carbide (FexC) can produce olefins with selectivity up to ∼60%, the fraction of methane is still rather high, and the required high reaction temperature (300-350 °C) typically causes coke deposition and fast deactivation. Recently, we discovered that Co2C nanoprisms with preferentially exposed facets of (020) and (101) can effectively produce olefins from syngas conversion under mild reaction conditions with high selectivity. The methane fraction was limited within 5%, and the product distribution deviated greatly from ASF statistic law. The catalytic performances of Co2C nanoprisms are completely different from that reported for the traditional FT process, exhibiting promising potential industrial application.This Account summarizes our progress in the development of Co2C nanoprisms for Fischer-Tropsch synthesis to olefins (FTO) with remarkable efficiencies and stability. The underlying mechanism for the observed unique catalytic behaviors was extensively explored by combining DFT calculation, kinetic measurements, and various spectroscopic and microscopic investigation. We also emphasize the following issues: particle size effect of Co2C, the promotional effect of alkali and Mn promoters, and the role of metal-support interaction (SMI) in fabricating supported Co2C nanoprisms. Specially, we briefly review the synthetic methods for different Co2C nanostructures. In addition, Co2C can also be applied as a nondissociative adsorption center for higher alcohol synthesis (HAS) via syngas conversion. We also discuss the construction of a Co0/Co2C interfacial catalyst for HAS and demonstrate how to tune the reaction network and strengthen CO nondissociative adsorption ability for efficient production of higher alcohols. We believe that the advances in the development of Co2C nanocatalysts described here present a critic step to produce chemicals through the FTS process.

Harnessing the Synergistic Interplay of Fischer‐Tropsch Synthesis (Fe‐Co) Bimetallic Oxides in Na‐FeMnCo/HZSM‐5 Composite Catalyst for Syngas Conversion to Aromatic Hydrocarbons

Preparation of Fe@Si/S-34 Catalysts and Its Catalytic Performance for Syngas to Olefins

High Selectivity to Aromatics by a Mg and Na Co-modified Catalyst in Direct Conversion of Syngas

A CoFe Bimetallic Catalyst for the Direct Conversion of Syngas to Olefins

Synergism of surface Co-rich activated carbon-supported bimetallic Co:Fe catalysts for Fischer-Tropsch synthesis

Strategic assembly of active phases on Co-Fe bimetallic catalysts for efficient Fischer-Tropsch synthesis

Cobalt Carbide Nanocatalysts for Efficient Syngas Conversion to Value-Added Chemicals with High Selectivity

Enhancing CO 2 hydrogenation performance via the synergistic effects of iron carbides and iron oxides

Construction of Synergistic Fe5C2/Co Heterostructured Nanoparticles As an Enhanced Low Temperature Fischer–Tropsch Synthesis Catalyst

Bifunctional Catalysts Composed of Low Silicon‐content SAPO‐34 Nanosheets and in 2 O 3 /zro 2 with Improved Performance for CO 2 Hydrogenation

A Core-Shell Structured Na/Fe@Co Bimetallic Catalyst for Light-Hydrocarbon Synthesis from CO2 Hydrogenation

Enhanced Conversion of Syngas to Gasoline-Range Hydrocarbons over Carbon Encapsulated Bimetallic FeMn Nanoparticles

Highly dispersed Co-based Fischer–Tropsch synthesis catalysts from metal–organic frameworks

Enhancing the synergism of Fe3O4 and Fe5C2 to improve the process of CO2 hydrogenation to olefines

Role of Residual CO Molecules in OX–ZEO Relay Catalysis for Syngas Direct Conversion

Surface Si decoration of ultrafine NaFeMn-Si catalyst enabling high Fe-phase electron density for effectively converting syngas to aromatics

Direct Transformation of Syngas to Aromatics over Na-Zn-Fe5C2 and Hierarchical HZSM-5 Tandem Catalysts

Direct Conversion of Syngas to Gasoline Ranged Olefins over Na Impellent Fe@NaZSM-5 Catalyst

Fabrication of Transition Metal (Mn, Co, Ni, Cu)‐Embedded Faveolate ZnFe2O4 Spinel Structure with Robust CO2 Hydrogenation into Value‐added C2+ Hydrocarbons

Fischer–Tropsch Synthesis: ZIF-8@ZIF-67-Derived Cobalt Nanoparticle-Embedded Nanocage Catalysts

MOFs-assisted synthesis of robust and efficient cobalt-based Fischer–Tropsch catalysts