Graphene oxidation and reduction in medium vacuum by an UV lamp at 365 nm wavelength
L. Torrisi M. Cutroneo B. Fazio S. Conoci G. Salvato A. Torrisi L. Silipigni a Department of Mathematics and Computer Sciences,Physical Sciences and Earth Sciences (MIFT),University of Messina,Messina,Italyb Istituto Nazionale di Fisica Nucleare,Sezione di Catania,Catania,Italyc Nuclear Physics Institute of the CAS,Husinec Řež,Czech Republicd URT Lab SENS,Beyond NANO,CNR DSFTM ME,Messina,Italye Dipartimento di Scienze Chimiche,Biologiche,Farmaceutiche,ed Ambientali,Università degli Studi di Messina,Messina,Italyf CNR-IPCF,Messina,Italyg CNR-IMM,Catania,Italy
DOI: https://doi.org/10.1080/10420150.2024.2346321
2024-06-04
Radiation Effects and Defects in Solids
Abstract:The time-dependent graphene oxide (GO) reduction in medium vacuum under ultraviolet (UV) irradiation at 365 nm has been investigated. We found that GO exposed to UV at room temperature and at a vacuum of about 10 −1 mbar shows a notable oxidation for irradiation times up to about 60 min followed by a successive reduction up to 210 min. Characterization measurements have been performed mainly using the Attenuated Total Reflectance (ATR) Fourier Transform Infrared (FTIR) and Raman spectroscopies. ATR-FTIR spectra, acquired in the (400–4000) cm −1 wavenumber range, have indicated an initial decrement of the IR transmission (oxidation process) with the exposure time up to about 60 min and a successive increase of the IR transmission (reduction process) for greater irradiation times up to 210 min. The IR transmission bands are attributed to the oxygen functional groups contained in GO which increase for low UV exposure times and gradually disappear during the UV-induced reduction process. Raman spectra confirm this interpretation showing a decrease of the A D /A G ratio value, with respect to the GO virgin value, for low UV exposure times and an increase for greater times. The GO oxidation and reduction processes, due to the UV GO treatment in medium vacuum conditions, have been also verified by energy dispersive X-ray fluorescence and surface wettability measurements
physics, condensed matter, fluids & plasmas,nuclear science & technology