Titanium-Containing Metal–Organic Framework Modified Separator for Advanced Lithium–Sulfur Batteries
Chu Qi,Lin Xu,Jia Wang,Huilan Li,Chengcheng Zhao,Lina Wang,Tianxi Liu
DOI: https://doi.org/10.1021/acssuschemeng.0c03536
2020-08-04
Abstract:The shuttling of polysulfide intermediates (Li<sub>2</sub>S<i><sub>n</sub></i>, 2 < <i>n</i> ≤ 8) and the dendrite growth on the Li-metal surface have blocked the practical applications of lithium–sulfur (Li–S) batteries. Functionalizing the separator provides a straightforward approach to address these issues. Herein, we demonstrate a multifunctional MIL-125(Ti)-modified polypropylene/polyethylene separator for advanced Li–S batteries. The MIL-125(Ti), a Ti-containing metal–organic framework (MOF), features an open-skeleton construction, a high intrinsic microporosity and a Lewis acid characteristic. Compared with pristine separator, that with MIL-125(Ti) coating shows better electrolyte wettability and less resistance. The unique coating layer acts as an effective physical and chemical barrier region to capture polysulfide species without affecting the smooth transport of Li<sup>+</sup>. Meanwhile, the highly ordered micropores with a diameter of ∼1.5 nm in the MOFs guide in a homogeneous Li<sup>+</sup> plating and thereby inhibit lithium dendrites. Consequently, the MOF-modified separator enables a significantly improved cycling stability and rate capability of the Li–S battery. The capacity retention of over 60% at 0.2 C (1 C = 1675 mA g<sup>–1</sup>) upon 200 cycles and a specific capacity of 612 mAh g<sup>–1</sup> at 2 C is realized. The facile approach offers an effective pathway toward high-performance Li–S batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c03536?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c03536</a>.Porosity measurement, calculated adsorption energy between polysulfides and MIL-125(Ti), polysulfide adsorption experiment, Ti 2p XPS spectrum of MIL-125(Ti), mechanical properties of separators, characterization of the separator after stretching, rate capability of Li–S cells, cyclic performance of Li–S cells at 0.2 C, comparison of different MOF-modified separators for Li–S batteries, morphology of bare Li anode, and performance of Li||Cu and Li||Li symmetric cells (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c03536/suppl_file/sc0c03536_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology