Room‐Temperature Symmetric Giant Positive and Negative Electrocaloric Effect in PbMg 0.5 W 0.5 O 3 Antiferroelectric Ceramic
Junjie Li,Hong‐Hui Wu,Jianting Li,Xiaopo Su,Ruowei Yin,Shiqiang Qin,Dong Guo,Yanjing Su,Lijie Qiao,Turab Lookman,Yang Bai
DOI: https://doi.org/10.1002/adfm.202101176
IF: 19
2021-06-12
Advanced Functional Materials
Abstract:<p>As an emerging solid-state refrigeration technology with zero-emission and high energy conversion efficiency, there is a compelling need for ferroelectric materials with giant electrocaloric effects (ECEs) at room temperature suitable for refrigeration applications. The complex perovskite antiferroelectric (AFE), PbMg<sub>0.5</sub>W<sub>0.5</sub>O<sub>3</sub>, containing non-equivalent B-site ions with a symmetric giant positive and negative ECE near room temperature is presented. At the Curie temperature of 36 °C, the first-order AFE–paraelectric phase transition gives rise to a large enthalpy change of 3.92 J g<sup>−1</sup>, more than four times that of BaTiO<sub>3</sub>. This leads to a significant ECE under the influence of an electric field. The direct electrocaloric characterization shows that the adiabatic temperature change, Δ<i>T</i>, exhibits symmetric peaks with a giant positive maximum of 1.79 K (Δ<i>S </i>= 1.68 J kg<sup>−1</sup> K<sup>−1</sup>) at 36 °C and a negative maximum of −2.02 K (Δ<i>S </i>= −1.93 J kg<sup>−1</sup> K<sup>−1</sup>) at 34 °C. The ultrahigh magnitude of Δ<i>T</i> near room temperature makes PbMg<sub>0.5</sub>W<sub>0.5</sub>O<sub>3</sub> a superior electrocaloric material far beyond traditional PbZrO<sub>3</sub>-based AFEs. The coexistence of symmetric giant positive and negative Δ<i>T</i> to further improve cooling efficiency is expected. In addition, the good reversibility and negligible leakage current should pave the way for practical applications.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology