Hot pressing process ameliorates internal defects of PBZ/PVDF composite film for a high electrocaloric effect near room temperature
Guoming Qian,Kongjun Zhu,Kang Yan,Jing Wang,Jinsong Liu,Zhong Yang,Weiqing Huang,Chuanxiang Zhang,Kan Bian
DOI: https://doi.org/10.1142/S1793604722510067
IF: 1.4901
2021-12-22
Functional Materials Letters
Abstract:The poor interface compatibility between inorganic fillers and organic polymer matrix in nanocomposite has presented considerable challenges, which limit the applicable electric field ranges and reduce the interface polarization interaction. In this paper, Pb 0.8 Ba 0.2 ZrO 3 (PBZ) nanofibers were introduced into the polyvinylidene fluoride (PVDF) matrix to prepare composite film, and the effect of hot pressing on interface compatibility was investigated at volume composite ratios of 3% and 4%. For the untreated film, Ps and E+ of the 3 vol.% composite film are 9.68 μ C/cm 2 and 401 MV/m, respectively, and those for the 4 vol.% composite film are 9.15 μ C/cm 2 and 408 MV/m, respectively. These differences are mainly due to the impact of internal defects. After hot pressing, Ps and E+ for the 3 vol.% composite film became 10.22 μ C/cm 2 and 490 MV/m, respectively. Those for the 4 vol.% composite film are 9.85 μ C/cm 2 and 485 MV/m. Experiment and simulation results showed the beneficial effect of hot pressing, which ameliorated poor interfacial compatibility, reduced internal defects, and improved the crystallinity of the composite film. A high electrocaloric effect (ECE) was obtained by using the direct measure method. At −30 ∘ C, the ΔT values of hot-pressed PBZ/PVDF film at 3 √ and 4 √ vol.% were 23.81 and 19.73 K, respectively. When temperature increased to 70 ∘ C, the ΔT values were 9.44 and 7.01 K, respectively, which were 1.58 times of the values of a non-hot-pressed film. These results indicated that hot pressing alleviated the interface problem and resulted in high EC performance under a high-strength electric field.
materials science, multidisciplinary