Bicomponent multifilament yarns of recycled poly(ethylene terephthalate) and nano-titanium dioxide for antibacterial carpet

Sommai Pivsa-Art,Komson Sunyikhan,Weraporn Pivsa-Art

DOI: https://doi.org/10.1177/15280837211011774

2021-05-06

Journal of Industrial Textiles

Abstract:Recycled poly(ethylene terephthalate) (RPET) multifilament yarns are used in carpet manufacturing as a way to reduce plastic waste. The conventional RPET carpet is however susceptible to bacterial accumulation. As a result, this research experimentally doped RPET with nano-structure titanium dioxide (nano-TiO 2 ) to produce RPET/nano-TiO 2 bicomponent multifilament yarns with antibacterial property. The experimental multifilament yarn structure consisted of two parts: neat RPET core and RPET/nano-TiO 2 shell. The nano-TiO 2 content in the shell was varied between 1 and 3 wt% and the core/shell (C/S) ratios between 90/10, 70/30, and 50/50 w/w. The effects of C/S ratio and nano-TiO 2 content on the mechanical and antibacterial properties of bicomponent multifilament yarns were determined. The experimental results indicated that the C/S ratio had no effect on the tenacity and elongation at break. Meanwhile, the tenacity and elongation at break of bicomponent fibers increased with nano-TiO 2 content in the shell. The TiO 2 -doped RPET bicomponent yarns effectively inhibited the growth of Escherichia coli and Staphylococcus aureus. The 90/10 bicomponent multifilament fiber with 3 wt% TiO 2 achieved the highest antibacterial activity. The very high antibacterial activity was attributable to greater deposition of nano-TiO 2 particles near and on the shell surface.

materials science, textiles