Preparation and Characterization of Carbon Based Composite Conductive Ink

Jieni Tian,Jiangping Yuan,Guangxue Chen,Weili Zhang

DOI: https://doi.org/10.1007/978-981-16-0503-1_91

2021-01-01

Abstract:The efficient dispersion of inorganic materials in organic polymers of composite conductive inks is the key challenge in formulating composite conductive inks. To this end, this paper presents a preparation of water-based composite conductive ink using carbon-based graphene oxide (GO) and poly 3,4-ethylenedioxythiophene (PEDOT: PSS) filler, and proposes a simple and stable personalized composite conductive ink formula based on the relative property performances. In order to improve the compatibility between PEDOT: PSS and GO, firstly, GO was pretreated with sulfuric acid at pH = 1 in a water bath, next the acidified GO solution was mixed with PEDOT: PSS as a conductive filler, and polyacrylic acid (PAA) was used as ink binder to prepare PEDOT/GO conductive ink. The results of key performance characterization show that the overall performance of the ink is the optimal, when its first ratio of the PEDOT to the binder is 4.8:1, and the second ratio of the GO to the PEDOT is 2.5‰.