Abstract:Phosphogypsum is an industrial waste generated in the production of fertilizers causing environmental problems. Calcined phosphogypsum (CPG) is obtained by low-temperature calcination and dehydration of phosphogypsum. CPG is mainly used to produce building materials. However, mechanical strength properties and water resistance of CPG materials is extremely poor, which leads to its relatively low utilization rate in construction industry. To address this issue, various amount of Ordinary Portland cement (OPC), fly ash (FA), rice husk (RH) and modified admixtures (AD) were mixed with the CPG to obtain CPG-based composite cementitious materials, which enhanced the water resistance and mechanical strength of the corresponding hardened materials. The influence of different contents of cement on the setting time, hydration heat, hydration products, mechanical properties, water absorption, heavy metal leaching and deterioration coefficient of the composite cementitious material is investigated. The results showed that the optimal mixing ratio of CPG: OPC: FA: RH was 57: 20: 10: 13 considering the water resistance and mechanical strength properties of CPG-based composite cementitious materials. On these conditions, the compressive strength, the flexural strength, water absorption and deterioration coefficient of the specimens at 28 days are 6.1 MPa, 4.6 MPa, 29.4% and 0.66 respectively, which were in line with the national standard of phosphorus building gypsum wallboard. It was demonstrated that two skeleton types are present in the samples prepared using CPG-based composite cementitious materials, which had a synergistic support effect on the structure. The first skeleton was formed by gypsum dihydrate crystals (CaSO 4 ·2H 2 O) and provided strength to the specimens at an early stage, while the second skeleton was formed by ettringite (AFt) and C–S–H gels, which provided strength at a later stage. The skeletons make the hardened materials denser and more waterproof. Moreover, the composite materials exhibited a positive solidification effect on heavy metals present in CPG.

Comparison of Strength Development in Waste Industrial Gypsum Produced by the Hemihydrate and Dihydrate Processes

Geotechnical properties of hemihydrate and dihydrate phosphogypsum

Effect of neutralization on the setting and hardening characters of hemihydrate phosphogypsum plaster

Experimental Study on the Material Characteristics of Slag Cement with Various Phosphogypsum Materials

Development and optimization of phosphogypsum-based geopolymer cement

Stress-Strain Behavior and Strength Development of High-Amount Phosphogypsum-Based Sustainable Cementitious Materials

Study on physical and chemical characteristics of β-hemihydrate phosphogypsum

Influence of treated waste phosphogypsum materials on the properties of ordinary portland cement

Potential use of phosphogypsum in concrete

Improving mechanical properties of hemihydrate phosphogypsum via alkali-activated mineral admixtures

A Sustainable Composite Cementitious Material Manufactured by Phosphogypsum Waste

Effect of calcination temperature and superplasticizer on the properties of anhydrite II from phosphogypsum

Effects of phosphogypsum on hydration properties and strength of calcium aluminate cement

Influence mechanism of alkaline environment on the hydration of hemihydrate phosphogypsum: A comparative study of various alkali

Thermal and Mechanical Properties Enhancement of Cement Mortar using Phosphogypsum Waste: Experimental and Modeling Study

Valorization of phosphogypsum as a road material: Stabilizing effect of fly ash and lime additives on strength and durability

Research on formulation optimization and hydration mechanism of phosphogypsum-based filling cementitious materials

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

Influence of cement on properties of calcined phosphogypsum based composite cementitious materials