Using a Self-Assembled Two-Dimensional MXene-Based Catalyst (2D-Ni@Ti 3 C 2 ) to Enhance Hydrogen Storage Properties of MgH 2
Wen Zhu,Subrata Panda,Chong Lu,Zhewen Ma,Darvaish Khan,Jinjian Dong,Fengzhan Sun,Hao Xu,Qiuyu Zhang,Jianxin Zou
DOI: https://doi.org/10.1021/acsami.0c12767
2020-11-03
Abstract:In this work, we report the remarkable catalytic effects of a novel Ti<sub>3</sub>C<sub>2</sub> MXene-based catalyst (), which was prepared via self-assembling of Ni nanoparticles onto the surface of exfoliated Ti<sub>3</sub>C<sub>2</sub> nanosheets. The resultant catalyst, characterized by ultradispersed Ni nanoparticles being anchored on the monolayer Ti<sub>3</sub>C<sub>2</sub> flakes, was introduced into MgH<sub>2</sub> through ball milling. <i>In situ</i> transmission electron microscopy (TEM) analysis revealed that a synergetic catalytic effect of multiphase components (Mg<sub>2</sub>Ni, TiO<sub>2</sub>, metallic Ti, etc.) derived in the MgH<sub>2</sub> + composite exhibits remarkable improvements in the hydrogen sorption kinetics of MgH<sub>2</sub>. In particular, the MgH<sub>2</sub> + composite can absorb 5.4 wt % H<sub>2</sub> in 25 s at 125 °C and release 5.2 wt % H<sub>2</sub> in 15 min at 250 °C. Interestingly, it can uptake 4 wt % H<sub>2</sub> in 5 h even at room temperature. Furthermore, the dehydrogenation peak temperature of the MgH<sub>2</sub> + composite is about 221 °C, which is 50 and 122 °C lower than that of MgH<sub>2</sub> + Ti-MX and MgH<sub>2</sub>, respectively. The excellent hydrogen sorption properties of the MgH<sub>2</sub> + composite are primarily attributed to the peculiar core–shell nanostructured MgH<sub>2</sub>@Mg<sub>2</sub>NiH<sub>4</sub> hybrid materials and the interfacial coupling effects from different catalyst–matrix interfaces. The results obtained in this study demonstrate that using self-assembling of transition-metal elements on two-dimensional (2D) materials as a catalyst is a promising approach to enhance the hydrogen storage properties of MgH<sub>2</sub>.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c12767?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c12767</a>.Figure S1: TEM analysis of the rehydrogenated MgH<sub>2</sub> + sample; Figure S2: EDS mapping of the rehydrogenated MgH<sub>2</sub> + sample; Figure S3: DSC profiles for MgH<sub>2</sub>, MgH<sub>2</sub> + Ti-MX, and MgH<sub>2</sub> + at different heating rates; and Figure S4: PC isotherms of the pristine MgH<sub>2</sub> and MgH<sub>2</sub> + composites at different temperatures; Table S1: summary of hydrogen sorption properties for the literature (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c12767/suppl_file/am0c12767_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology