The reduction of U(VI) on corroded iron under anoxic conditions

Daqing Cui,Kastriot Spahiu

DOI: https://doi.org/10.1524/ract.2002.90.9-11_2002.623

2002-09-01

Radiochimica Acta

Abstract:Summary The corrosion of iron and the interaction between corroded iron and U(VI) in anoxic conditions were investigated. The anoxic conditions were obtained by flushing an 99.97% Ar-0.03% CO 2 gas mixture through the test vessel, in which an oxygen trap and six reaction bottles containing synthetic groundwater (10 mM NaCl and 2 mM HCO 3 − .) were placed. The dark-green coloured corrosion product, formed on iron surface after three months corrosion in synthetic groundwater solutions, was identified by powder X-ray diffraction to be carbonate green rust, Fe 4 II Fe 2 III (OH) 12 CO 3 . The iron foil that reacted in a solution (10 ppm U(VI), 10 mM NaCl and 2 mM HCO 3 − ) for three months was analysed by SEM-EDS. The result shows that: (i) an uneven layer of carbonate green rust (1-5 μm thick) formed on the metallic iron; (ii) a thin (0.3 μm) uranium-rich layer deposited on top of the carbonate green rust layer; and (iii) some UO 2 crystals (3-5 μm sized) on the thin uranium layer. The experimental results proved that the U(VI) removal capacity of metal iron is not hindered by formation of a layer of carbonate green rust on the iron. Tests with cast iron and pure iron indicate that they have similar U(VI) removal capacities. At the end of experiment, U concentrations in solution approached the solubility of UO 2 (s), 10 −8 M. The stability of the carbonate green rust at the experimental conditions, pH, E h , [Fe 2+ ] and [HCO 3 − ], is discussed.

chemistry, inorganic & nuclear,nuclear science & technology