In-situ Studies of Stress- and Magnetic-Field-induced Phase Transformation in a Polymer-Bonded Ni–Co–Mn–In Composite
D. M. Liu,Z. H. Nie,G. Wang,Y. D. Wang,D. E. Brown,J. Pearson,P. K. Liaw,Y. Ren
DOI: https://doi.org/10.1016/j.msea.2010.02.034
IF: 6.044
2010-01-01
Materials Science and Engineering A
Abstract:A polymer-bonded Ni45Co5Mn36.6In13.4 ferromagnetic shape–memory composite was fabricated, having magnetic-field-driven shape recovery properties. The thermo-magnetization curves of the composite suggested that the magnetic-field-induced reverse martensitic transformation occurs in the composite. The effects of temperature, stress, and magnetic-field on the phase transformation properties were systematically investigated using an in-situ high-energy X-ray diffraction technique. A temperature-induced reversible martensitic phase transformation was confirmed within the composite, showing a broad phase transformation interval. Stress-induced highly textured martensite was observed in the composite during uniaxial compressive loading, with a residual strain after unloading. The origin of the textured martensite can be explained by the grain-orientation-dependent Bain distortion energy. A recovery strain of ∼1.76% along the compression direction was evidenced in the pre-strained composite with an applied magnetic-field of 5T. This recovery was caused by the magnetic-field-induced reverse martensitic phase transformation. The phase transformation properties of the ferromagnetic shape–memory composite, different from its bulk alloys, can be well explained by the Clausius–Clapeyron relation. The large magnetic-field-induced strain, together with good ductility and low cost, make the polymer-bonded Ni–Co–Mn–In composites potential candidates for magnetic-field-driven actuators.