Elastic properties and radiation shielding ability of ZnO–P2O5/B2O3 glass system

Miysoon A. Alothman,Z. A. Alrowaili,Ateyyah M. Al-Baradi,Ozge Kilicoglu,C. Mutuwong,M. S. Al-Buriahi

DOI: https://doi.org/10.1007/s10854-021-06442-z

2021-06-29

Abstract:This paper focuses on the elastic properties and radiation shielding ability of ZnO–P₂O₅/B₂O₃ glass system containing six samples named as ZBP1, ZBP2, ZBP3, ZBP4, ZBP5, and ZBP6. For ZBP1, ZBP2, ZBP3, and ZBP4 samples, we investigated the influence of ZnO/P₂O₅ substitution (with absence of B₂O₃), while the effect of P₂O₅/B₂O₃ substitution was studied and discussed for ZBP5, and ZBP6 samples. The findings indicate that the Young′s modulus (<i>E</i>_th) as well as Bulk modulus (<i>K</i>_th) and Shear modulus (<i>S</i>_th) increased under both the ZnO/P₂O₅ substitution and the P₂O₅/B₂O₃ substitution. The values of gamma constant (<i>Γ</i>) rise with growing energy levels and the highest <i>Γ</i> was observed around 10 MeV and they were of 111,33, 111,83,116,60,119,69,119,86,120,57 R.m²/Ci.h for the investigated glasses of ZBP1- ZBP2- ZBP3- ZBP4- ZBP5 and ZBP6, respectively. The stopping power (SP) for electron was around 3.30 MeV cm²/g at the energy of 0.1 MeV for all of the involved glasses. The maximum cross section for fast neutron was observed for ZBP6 with the value of 0.11432 cm⁻¹. The ZBP6 sample has the best properties among the other investigated samples for shielding applications.