Preparation of backfill materials by solidifying municipal solid waste incineration fly ash with slag-based cementitious materials

K. Wang,K. Li,X. Huang,W. Ni,S. Zhang
DOI: https://doi.org/10.1007/s13762-022-04138-3
2022-04-09
International Journal of Environmental Science and Technology
Abstract:In this study, solid waste granulated blast furnace slag and flue gas desulfurization gypsum were used to solidify municipal solid waste incineration fly ash to prepare cement-free backfill material. It was found that appropriate concentrations of fly ash (30 wt%) in backfill materials improved its mechanical strength, fluidity and rheological properties, as well as reducing the setting time, the ratio of bleeding and heavy metals leaching; shrinkage during drying was also restrained. XRD, FTIR and SEM results indicate that, under the action of OH− in fly ash, depolymerization of surface alumina and silica structures of slag occurred, and a large volume of silicon-oxygen and aluminum-oxygen tetrahedra were released in the pore solution, forming [Ca2Al(OH)6·2H2O]+. In sample M10, the hydration reaction of SO42− from desulfurization gypsum and [Ca2Al(OH)6·2H2O]+ resulted in the formation of ettringite due to the incorporation of insufficient fly ash. When the volume of fly ash increased, the alkaline environment improved the activity of the slag, the hydration reaction was favored by Cl− from fly ash, and ettringite and Friedel's salt co-existed in the cementitious system. With a further increase in fly-ash content, almost all [Ca2Al(OH)6·2H2O]+ released by slag reacted with Cl− rather than SO42− to produce Friedel's salt due to the small molecular size of Cl−, which are more prone to react with [Ca2Al(OH)6·2H2O]+, while ettringite disappeared. This study used solid waste to stabilize fly ash for the preparation of backfill material providing a new solution for fly-ash disposal, as well as providing an innovative method for low-cost and sustainable restoration of mine areas.
environmental sciences
What problem does this paper attempt to address?