Improvement of Mechanical and Wear Resistance of Natural Fiber Reinforced Polymer Composites Through Synthetic Fiber (Glass/Carbon) Hybridization

Subhrajyoti Saroj,Ramesh Kumar Nayak

DOI: https://doi.org/10.1007/s12666-021-02347-x

2021-07-12

Transactions of the Indian Institute of Metals

Abstract:<p class="a-plus-plus">Natural fiber-reinforced polymer (NFRP) composites are biodegradable materials than synthetic fiber such as glass and carbon fiber reinforced polymer composites. However, due to the lower mechanical properties of NFRP composites, application in structural components is limited. Therefore, the present investigation focuses on the effect of carbon and glass fiber hybridization with flax and Kenaf fiber on tribo-mechanical properties of the hybrid composites. Four types of hybrid composites (C<sub class="a-plus-plus">2</sub>F<sub class="a-plus-plus">3</sub>C<sub class="a-plus-plus">2</sub>, C<sub class="a-plus-plus">2</sub>K<sub class="a-plus-plus">3</sub>C<sub class="a-plus-plus">2</sub>, G<sub class="a-plus-plus">2</sub>F<sub class="a-plus-plus">3</sub>G<sub class="a-plus-plus">2</sub> and G<sub class="a-plus-plus">2</sub>K<sub class="a-plus-plus">3</sub>G<sub class="a-plus-plus">2</sub>) and plain glass, carbon, flax and kenaf fiber reinforced polymer composites are fabricated by hand lay-up method. The results reveal that flax fiber hybridization with carbon fiber (C<sub class="a-plus-plus">2</sub>F<sub class="a-plus-plus">3</sub>C<sub class="a-plus-plus">2</sub>) gives the best hybrid effect and improves its flexural strength (364.4 ± 15.0 MPa), modulus (24.7 ± 1.4GPa), and Izod impact strength (26.5 ± 2.4 kJ/m<sup class="a-plus-plus">2</sup>). However, Kenaf fiber hybridization with glass fiber (G<sub class="a-plus-plus">2</sub>K<sub class="a-plus-plus">3</sub>G<sub class="a-plus-plus">2</sub>) gives optimum flexural strength (335.6 ± 33.2 MPa), modulus (17.2 ± 0.9GPa), and Izod impact strength (80.2 ± 16.0 kJ/m<sup class="a-plus-plus">2</sup>). Kenaf fiber reinforced polymer hybrid composites (G<sub class="a-plus-plus">2</sub>K<sub class="a-plus-plus">3</sub>G<sub class="a-plus-plus">2</sub>) show the lowest abrasive specific wear rate (21.9 ± 0.9mm<sup class="a-plus-plus">3</sup>/Nm) compared to other hybrid composites. Furthermore, the fractography analysis of hybrid composites is carried out using scanning electron microscopy to make possible structure–property co-relationship.</p>

metallurgy & metallurgical engineering