Abstract:The high cost of precursors and the complexity of synthesis procedures have hindered the widespread use of two-dimensional (2D) porous carbon nanosheets in water splitting. In this study, we successfully developed a low-cost method for the rapid synthesis of three-dimensional (3D) hierarchically porous architectures self-assembled from iron–copper nanoparticles embedded in boron (B)/nitrogen (N)-codoped 2D porous carbon nanosheets (denoted as FeCu@BNPCNS). The optimal FeCu@BNPCNS-900 nanosheet exhibited a large surface area, abundant porous channels, meso/macropores, and carbon edges/defects. Particularly, 10.25 atom% of B/N electrochemically active centers (such as pyridinic-N (including the metal–nitrogen–carbon species), pyrrolic-N, graphitic-N, and BC 3 ) were successfully doped into the optimal FeCu@BNPCNS-900 nanosheets. In an alkaline solution, FeCu@BNPCNS-900 exhibited excellent electrocatalytic activity for hydrogen evolution reaction (HER), which was higher than that of the commercial 20 wt% Pt/C. For example, the HER potential of FeCu@BNPCNS-900 at 10 mA cm −2 [ E 10 ; −202.3 mV vs. reversible hydrogen electrode (RHE)] was only 140.2 mV more negative than that of 20 wt% Pt/C (−62.1 mV vs. RHE). Additionally, FeCu@BNPCNS-900 exhibited a slightly lower oxygen evolution reaction (OER) electrocatalytic activity than the ruthenium oxide (RuO 2 ). Particularly, the OER E 10 potential (+1.634 V vs. RHE) of FeCu@BNPCNS-900 was only 76 mV more positive than that of RuO 2 (+1.558 V vs. RHE). The FeCu@BNPCNS-900||FeCu@BNPCNS-900 cell achieved 10 mA cm −2 at 1.613 V, which was 58 mV more negative than that of the 20 wt% Pt/C||RuO 2 cell (1.671 V). The excellent water-splitting performance of FeCu@BNPCNS-900 could be attributed to the 3D hierarchically porous architecture, abundant channels/mesopores, and uniformly dispersed electrocatalytically active sites. Therefore, we developed an efficient strategy for the large-scale and low-cost synthesis of 2D porous carbon nanosheets without the need for precursors, templates, or surfactants.

Bottom-up synthesis of semiconductive carbonaceous nanosheets on hematite photoanode for photoelectrochemical water splitting

The role of carbon dots - derived underlayer in hematite photoanodes

Synthesis of a Cu2O/Carbon Film/NiCoB‐Grpahene Oxide Heterostructure As Photocathode for Photoelectrochemical Water Splitting

Millisecond Synthesis of CoS Nanoparticles for Highly Efficient Overall Water Splitting

Solution-phase conversion of glucose into semiconductive carbonaceous nanosheet photocatalysts for enhanced environmental applications

Constructing Chemical Interaction between Hematite and Carbon Nanosheets with Single Active Sites for Efficient Photo‐Electrochemical Water Oxidation

Ultrathin NiMn-layered Double Hydroxide Nanosheets Coupled with Α-Fe2o3 Nanorod Arrays for Photoelectrochemical Water Splitting

Template-free synthesis of hematite photoanodes with nanostructured ATO conductive underlayer for PEC water splitting.

Integrated Hierarchical Cobalt Sulfide/Nickel Selenide Hybrid Nanosheets As an Efficient Three-dimensional Electrode for Electrochemical and Photoelectrochemical Water Splitting.

FeSe2/CoSe Nanosheets for Efficient Overall Water Splitting under Low Cell Voltages

Surface Engineered Doping of Hematite Nanorod Arrays for Improved Photoelectrochemical Water Splitting

Chelation-mediated in-situ formation of ultrathin cobalt (oxy)hydroxides on hematite photoanode towards enhanced photoelectrochemical water oxidation

High-density defect-induced ultrahigh boron and nitrogen doping of iron–copper-functionalized porous carbon nanosheets for enhanced water splitting

Facile Solution Synthesis of Α-Fef3·3h2o Nanowires and Their Conversion to Α-Fe2o3 Nanowires for Photoelectrochemical Application

Novel Composites of Α‐fe2o3 Tetrakaidecahedron and Graphene Oxide As an Effective Photoelectrode with Enhanced Photocurrent Performances

Facile Growth Of Porous Hematite Films For Photoelectrochemical Water Splitting

Nanocarbon-Enhanced 2D Photoelectrodes: A New Paradigm in Photoelectrochemical Water Splitting

Ultrathin MOF Coupling with Molecular Cobaloxime to Construct an Efficient Hybrid Hematite Photoanode for Photocatalytic Water Splitting

Bottom-up Fabrication of Graphitic Carbon Nitride Nanosheets Modified with Porphyrin Via Covalent Bonding for Photocatalytic H 2 Evolution

Deposition of FeOOH Layer on Ultrathin Hematite Nanoflakes to Promote Photoelectrochemical Water Splitting

In-situ synthesis of Fe phosphate layer on the porous hematite nanocube for efficient photoelectrochemical water splitting