Tuning the Structural Isomers of Phenylenediammonium Cations to Afford Efficient and Stable Perovskite Solar Cells and Modules

Cheng Liu,Yi Yang,Kasparas Rakstys,Arup Mahata,Marius Franckevicius,Edoardo Mosconi,Raminta Skackauskaite,Bin Ding,Onovbaramwen Jennifer Usiobo,Jean-Nicolas Audinot,Hiroyuki Kanda,Simonas Driukas,Gabriele Kavaliauskaite,Vidmantas Gulbinas,Marc Dessimoz,Vytautas Getautis,Filippo De Angelis,Yong Ding,SongYuan Dai,Paul Dyson,Mohammad Khaja Nazeeruddin

DOI: https://doi.org/10.21203/rs.3.rs-711763/v1

2021-07-21

Abstract:Abstract Organic halide salt passivation is considered to be an essential strategy to reduce defects in state-of-the-art perovskite solar cells (PSCs). This strategy, however, suffers from the inevitable formation of in-plane favored two-dimensional (2D) perovskite layers with impaired charge transport, especially under thermal conditions, impeding photovoltaic performance and device scale-up. To overcome this limitation, we studied the energy barrier of 2D perovskite formation from ortho- , meta- and para- isomers of (phenylene)di(ethylammonium) iodide (PDEAI 2 ) that were designed for tailored defect passivation. Treatment with the most sterically hindered ortho -isomer not only prevents the formation of surficial 2D perovskite film, even at elevated temperatures, but also maximizes the passivation effect on both shallow- and deep-level defects. The ensuing PSCs achieve an efficiency of 23.9% with long-term operational stability (over 1000 hours). Importantly, a record efficiency of 21.4% for the perovskite module with an active area of 26 cm 2 was achieved.