Study of hybrid organic–inorganic halide perovskite solar cells based on MAI[(PbI2)1−x(CuI)x] absorber layers and their long-term stability

Wissal Belayachi,Salma Boujmiraz,Salma Zouhair,Kübra Yaşaroğlu,Guy Schmerber,Jean-Luc Rehspringer,Thomas Fix,Abdelilah Slaoui,Mohammed Abd-Lefdil,Aziz Dinia

DOI: https://doi.org/10.1007/s10854-021-06582-2

2021-07-17

Abstract:<p class="a-plus-plus">One of the major perovskites used as a light absorber in perovskite solar cells (PSCs) is methylammonium lead iodide (MAPI). MAPI perovskite shows many optimal optoelectronic properties making it a high-performance solar cell material. Nonetheless, PSCs face some limitations related to stability and degradation against moisture, and toxicity due their lead content. The goal of this work is to study the partial substitution of lead iodide (PbI<sub class="a-plus-plus">2</sub>) with the inorganic compound copper iodide (CuI) to enhance the solar cell stability thanks to the hydrophobic properties of the latter. XRD showed a tetragonal crystal structure growth for the MAI[(PbI<sub class="a-plus-plus">2</sub>)<sub class="a-plus-plus">1−x</sub>(CuI)<sub class="a-plus-plus">x</sub>] perovskite films. Even for 20 mol%, CuI was well incorporated into the perovskite lattice structure producing a slight change in the lattice parameters. SEM analysis showed a clear improvement of the film's morphology with the CuI substitution (less pinholes, better uniformity). The optical absorption edges and calculated optical bandgap, around 1.55 eV, remain unchanged with CuI partial substitution. With the increase in CuI/PbI<sub class="a-plus-plus">2</sub> ratio photovoltaic properties of the MAI[(PbI<sub class="a-plus-plus">2</sub>)<sub class="a-plus-plus">1−x</sub>(CuI)<sub class="a-plus-plus">x</sub>] devices improved, higher <em class="a-plus-plus">V</em><sub class="a-plus-plus">OC</sub> and <em class="a-plus-plus">J</em><sub class="a-plus-plus">SC</sub> are observed. Finally, the stability was studied during 150 days in air and an enhancement of PSCs properties was observed for CuI substituted PbI<sub class="a-plus-plus">2</sub> PSCs.</p>

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied