Surface‐Integrating Oxygen Vacancy and CuxO Nanodots Enabling Synergistic Electric Field and Dual Catalytic Sites Boosting CO2 Photoreduction
Shuguan Li,Jingcong Hu,Fang Chen,Shengqi Chu,Ruofei Tang,Shengyao Wang,Qi An,Hongwei Huang
DOI: https://doi.org/10.1002/smll.202402882
IF: 13.3
2024-05-23
Small
Abstract:Surface‐integrated oxygen vacancies (Ov) and CuxO (1 < x < 2) nanodots below 10 nm enable the formation of enhanced internal electric field and cooperatively reduce the surface work function of Bi2MoO6, accelerating the separation of photocharge carriers. They also serve as dual catalytic sites to strengthen the activation CO2 into *CO2, considerably boosting the CO2 conversion process over Bi2MoO6, thus resulting in a remarkable CO generation rate increase of ≈15 times. High carrier separation efficiency and rapid surface catalytic reaction are crucial for enhancing catalytic CO2 photoreduction reaction. Herein, integrated surface decoration strategy with oxygen vacancies (Ov) and anchoring CuxO (1 < x < 2) nanodots below 10 nm is realized on Bi2MoO6 for promoting CO2 photoreduction performance. The charge interaction between Ov and anchored CuxO enables the formation of enhanced internal electric field, which provides a strong driving force for accelerating the separation of photocharge carriers on the surface of Bi2MoO6 (ηsurf ≈71%). They can also cooperatively reduce the surface work function of Bi2MoO6, facilitating the migration of carrier to the surface. Meanwhile, surface‐integrated Ov and CuxO nanodots allowing dual catalytic sites strengthens the adsorption and activation CO2 into *CO2 over Bi2MoO6, considerably boosting the progression of CO2 conversion process. In the absence of co‐catalyst or sacrificial agent, Bi2MoO6 with Ov and CuxO nanodots achieves a photocatalytic CO generation rate of 12.75 μmol g−1 h−1, a remarkable increase of over ≈15 times that of the original counterpart. This work provides a new idea for governing charge movement behaviors and catalytic reaction thermodynamics on the basis of synergistic improvement of electric field and active sites by coupling of the internal defects and external species.
materials science, multidisciplinary,nanoscience & nanotechnology,physics, applied,chemistry, physical, condensed matter