Abstract:Granular, microgel-based materials have garnered interest as promising tissue engineering scaffolds due to their inherent porosity, which can promote cell infiltration. Adapting these materials for 3D bioprinting, while maintaining sufficient void space to enable cell migration, can be challenging, since the rheological properties that determine printability are strongly influenced by microgel packing and void fraction. In this work, a strategy is proposed to decouple printability and void fraction by blending UV-crosslinkable gelatin methacryloyl (GelMA) microgels with sacrificial gelatin microgels to form composite inks. It is observed that inks with an apparent viscosity greater than ≈100 Pa s (corresponding to microgel concentrations ≥5 wt%) have rheological properties that enable extrusion-based printing of multilayered structures in air. By altering the ratio of GelMA to sacrificial gelatin microgels, while holding total concentration constant at 6 wt%, a family of GelMA:gelatin microgel inks is created that allows for tuning of void fraction from 0.20 to 0.57. Furthermore, human umbilical vein endothelial cells (HUVEC) seeded onto printed constructs are observed to migrate into granular inks in a void fraction-dependent manner. Thus, the family of microgel inks holds promise for use in 3D printing and tissue engineering applications that rely upon cell infiltration.

What problem does this paper attempt to address?

The key problem that this paper attempts to solve is how to achieve precise regulation of the void fraction of microgel scaffolds in 3D bioprinting while maintaining the printability of the materials. Specifically, the authors proposed a method of preparing composite inks by mixing photocrosslinkable gelatin methacrylamide (GelMA) microgels and sacrificial gelatin microgels to achieve these two goals. ### Summary of Main Problems 1. **Void Fraction and Cell Infiltration**: - Void fraction is an important factor affecting cell migration, infiltration, and nutrient diffusion. A high void fraction can promote cell infiltration and function maintenance, but usually reduces the mechanical properties and printability of the materials. 2. **Printability of Materials**: - In order to achieve 3D bioprinting, the materials must have appropriate rheological properties (such as shear - thinning behavior) to ensure that they can be extruded through a fine nozzle and form a stable structure. ### Solutions The authors solved the above problems through the following strategies: - **Introduction of Sacrificial Gelatin Microgels**: These microgels can be removed by temperature control after printing, thereby adjusting the void fraction of the final structure without changing the overall microgel concentration. - **Adjustment of Microgel Proportions**: By changing the ratio of GelMA microgels to sacrificial gelatin microgels, the void fraction can be regulated from 0.20 to 0.57 while maintaining the total microgel concentration unchanged. - **Optimization of Rheological Properties**: It was found that when the microgel concentration reaches 6 wt%, the ink has ideal rheological properties and can achieve good printability and shape fidelity. ### Experimental Verification To verify the biological relevance of this composite ink, the researchers inoculated human umbilical vein endothelial cells (HUVEC) onto the printed structures and observed that cell migration behavior depends on the void fraction. In addition, they also demonstrated the application potential of this technology in multi - material printing, enabling the patterned design of different void fractions in a single printed structure. ### Conclusion This study achieved the decoupling of the printability of microgel inks and the void fraction of printed scaffolds in 3D bioprinting for the first time, providing new possibilities for tissue engineering applications. By regulating the void fraction, the researchers were able to design 3D - printed scaffolds with a controllable endothelial cell infiltration rate and demonstrated the ability to form different void fraction patterns in multi - material printing. This strategy will help to improve the design flexibility and functionality of bioprinted scaffolds.

3D Printing of Microgel Scaffolds with Tunable Void Fraction to Promote Cell Infiltration