Abstract:Lightweight foamed concrete (LFC) made from cementitious materials with air pores entrapped in the matrix by mechanically entrained foam in the mortar slurry has several economic and environmental benefits. Most recently, LFC has been heralded as the next generation of lightweight construction industry concrete because of its versatility and technological advancements. Owing to its many desirable qualities, including low density, low cost, low thermal conductivity, low dimensional change, amazing load-bearing capacity, great workability, and low weight, it is considered an adaptable and flexible construction material. Given that LFC is a brittle building material and since fire is among the most frequent catastrophes to affect structures, it is crucial to consider the structural performance of LFC subjected to high temperatures. Hence, this experiment attempts to ascertain the effect of varying elevated temperatures on the LFC’s strength properties. Three LFC densities of 500, 1000 and 1500 kg/m3 were prepared. The LFC specimens were exposed to predetermined ambient and elevated temperatures of 20, 100, 200, 300, 400, 500, 600, 700 and 800 °C, and the LFC samples were assessed for porosity, compressive and flexural strengths. The outcomes of this investigation showed that, regardless of density, the loss of LFC stiffness exposed to elevated temperatures happened primarily after 90 °C. This shows that the underlying process triggering stiffness loss is internal cracking, that transpires when water grows and dissolves from a porous medium. Lowering the LFC dry density diminishes its strength and rigidity. The LFC-normalized strength and stiffness–temperature relationships of various dry densities, on the other hand, are very comparable. From ambient temperature up until 400 °C, all densities exhibit a moderate and constant loss in strength and stiffness. Nevertheless, the decline is faster up to 600 °C or 800 °C, at which point it loses its ability to support any given weight. This study emphasized the necessity for more study and codes’ provisions that take into consideration various LFC constituent types and cutting-edge construction material technologies.

Compressive and thermal properties of foamed concrete at high temperature

Compressive Behavior of Lightweight Concrete Using Aerogel-Reinforced Expanded Polystyrene Foams

Physical and mechanical properties of expanded vermiculite (EV) embedded foam concrete subjected to elevated temperatures

Residual durability, mechanical, and microstructural properties of foamed concrete subjected to various elevated temperatures

Preparation and Properties of Foam Concrete Incorporating Fly Ash

Experimental Research on Dynamic Mechanical Properties of High-Density Foamed Concrete

Effect of Foaming Agent, Binder and Density on the Compressive Strength and Thermal Conductivity of Ultra-Light Foam Concrete

Dynamic impact compressive performance of expanded polystyrene (EPS)-foamed concrete

Influence of bottom ash and polypropylene fibers on the physico-mechanical, durability and thermal performance of foam concrete: An experimental investigation

Influence of expanded vermiculite powder and silica fume on properties of foam concretes

The influence of foams, having different expansion ratios, on the structurization of thermal insulation foam concrete

Fire Resistance of Foamed Concrete for Discontinuous Partition Filling

Effect of polyethylene powder and heating treatment on the microstructure and hardened properties of foam concrete

Evaluation of the Mechanical Properties of Lightweight Foamed Concrete at Varying Elevated Temperatures

Effects of Mixing Techniques and Material Compositions on the Compressive Strength and Thermal Conductivity of Ultra-Lightweight Foam Concrete

Mechanical and Thermophysical Properties of Composite Wall with Foamed Concrete(1)

Residual compressive strength of EPS lightweight concrete under heating–air cooling regime

Thermal Insulation Properties and Simulation Analysis of Foam Concrete Regulated by Mechanical and Chemical Foaming

Experimental Scrutiny of Uniaxial Compressive Stress–Strain Relationship for Expanded Polystyrene Concrete

Investigating the Mechanical and Durability Characteristics of Fly Ash Foam Concrete

Influencing factors of mechanical and thermal conductivity of foamed phosphogypsum-based composite cementitious materials