Abstract:For an accurate estimation of the fatigue performance of welded joints, not only the initial residual stress field but also its variation under load is decisive. The portion of residual stress which stays stable can shift the load stress range much the same way as the mean stresses do in fatigue loading. The relaxation of residual stresses during fatigue loading however reduces this hazard to the structural health. That is, before considering the influence of residual stresses in fatigue, the effect of fatigue on residual stresses should be understood. In this work, the influence of the quasi-static and cyclic loading on the relaxation of welding residual stresses in small specimens and large components out of different steels namely S235JRG2, S355J2G3, P460NL, S690QL, S960QL, and S1100QL has been investigated experimentally. X-ray diffraction analysis as a reliable method has been used for the determination of residual stress profiles in surface layers. For residual stress analysis in deeper layers, synchrotron and neutron diffraction techniques were applied as complementary methods. A clear recognition of the difference between initial welding residual stresses in small- and large-scale specimens was observed. Tensile residual stresses as high as the yield strength could appear in large-scale welded specimens. That was not the case for small-scale welds due to the low grade of restraint. Nevertheless, in both types of samples, the highest residual stresses were obtained in the weld centerline. At the weld toe which is critical regarding fatigue crack initiation, the magnitude of the residual stresses is lower. Beside of that, it was observed that in the case of relaxation, the first load cycles especially in components out of low-strength steels are decisive. The influence of loading conditions and local mechanical properties on the relaxation of welding residual stresses was investigated based on principles of solid mechanics. The von Mises failure criterion was able to describe the relaxation behavior.

The Influence of Vibratory Treatment on the Fatigue Life of Welds: A Comparison with Thermal Stress Relief

Vibration Stress Relief Mechanism and Its Impact on Fatigue Life

Research on High-Frequency Vibratory Stress Relief of Small Cr12mov Quenched Specimens

Effects of heat and vibration treatments for welding on residual stresses and mechanical properties

Influence Of Vibration On Mechanical Properties Of Electroslag Welded Joint

The effect of residual stress on fatigue life of welded Cruciform joints of 16MnR for train bogie

Reduce the Residual Stress of Welded Structures by Post-Weld Vibration

Experimental and simulation analysis on the effect of vibratory stress relief on impact toughness of Q345/316 L dissimilar steel welded joints

Quantification of CTOD fracture toughness in welded joints to evaluate the efficacy of vibration stress relief compared to thermal stress relief

A combined computational and experimental study on vibration stress relief for large welded DH36 steel tube

The Application of Vibratory Stress Relief to Energy Engineering

Prediction of weld induced residual stress reduction by vibration of a T-joint using finite element method

The Boom of the Welding Residual Stress Aging Treatment

A Study on the Microstructure and Fatigue Properties of Welding Joints in Vibration‐Assisted Laser Welding Process

Fatigue behavior of SMA490BW welded components considering AHT with traction structural stress

The Effectiveness Evaluation of 314L Stainless Steel Vibratory Stress Relief by Dynamic Stress

Welding residual stress behavior under mechanical loading

Influence of post-weld heat treatment on welding residual stress in U-rib-to-deck joint

Vibration Stress Relief of DH 36 Rectangle Welded Plates

A practical analysis of residual stresses induced by high-frequency mechanical impact post-weld treatment

Synergetic Effects of Macro- and Microscopic Residual Stresses Induced by High-Frequency Mechanical Impact Post-weld Treatment on Fatigue Strength Enhancement of S335 Steel T-Weld