Carbazole-Modified Blue Light-Emitting Copolymers with the Backbones Integrated by Diphenyloxadiazole, Fluorene, and Triphenylamine
Ying Lin,Yu Chen,Tengling Ye,Dongge Ma,Yongxi Li
DOI: https://doi.org/10.1016/j.eurpolymj.2011.12.004
2012-01-01
Abstract:Two new blue light-emitting polymers, poly{[2,5-bis(4-phenylene)-1,3,4-oxadiazole]-[9,9-dihexylfluorene-2,7-diyl]-[N-(4-(9H-carbazol-9-yl)phenyl)-N,N-bis(p-phenylene)aniline]} (POFPA) and poly{[2,5-bis(4-phenylene)-1,3,4-oxadiazole]-[9,9-dihexylfluorene-2,7-diyl]-[4-(3,6-(di-9H-carbazol-9-yl)-9H-carbazol-9-yl)-N,N-bis(p-phenylene)-aniline]} (POFCPA), were synthesized by Suzuki coupling reactions. By GPC analysis against a linear polystyrene standard POFPA and POFCPA were found to have Mn of 1.68×104 and 3.70×103, respectively. In contrast to POFPA, the main absorption peak of POFCPA in dilute toluene solution was blue-shifted by Δλ=26nm owing to its backbone of relatively shorter π-conjugation length and more carbazole units in side chain. The absolute fluorescence quantum yield (Φf) of POFCPA in dilute toluene solution was determined as 73%, much higher than that of POFPA (Φf≈58.9%) measured under the same conditions. An electroluminescence device based on POFCPA displays a stable blue emission having color coordinates of (0.15, 0.20), a maximum brightness of 4762cd/m2, and a maximum current efficiency of 1.79cd/A. By using this polymer as the host material doped with 1wt.% 4,4′-bis[2-(4-(N,N-diphenylamino)phenyl)vinyl]biphenyl, the achieved highest brightness, maximum current efficiency and maximum power efficiency are 13,613cd/m2, 3.38cd/A, and1.84lm/W, respectively.