Highly Efficient Low-Pt-Based Electrocatalysts with Pt Single-Atom Active Sites for Oxygen Reduction Reaction
Jing Liu,JeongHan Roh,DongHoon Song,Junu Bak,Hyo-Jong Kim,Eun Ae Cho
DOI: https://doi.org/10.1149/ma2020-01381688mtgabs
2020-01-01
ECS Meeting Abstracts
Abstract:Platinum (Pt) has been preferred as the most viable catalytic material to accelerate the sluggish oxygen reduction reaction (ORR) in proton exchange membrane fuel cells (PEMFCs)1,2. However, the scarcity of Pt on earth makes it expensive, resulting in a concomitantly high cost for the commercial implementation of fuel cells. In this respect, significant efforts have been made worldwide to reduce Pt loading while retaining and even improving their high catalytic performance of Pt-based ORR electrocatalysts3,4. One of the effective approaches to improve the utilization efficiency of Pt atoms is to reduce the size of Pt nanoparticles to clusters or even to single atoms. Smaller Pt particles have higher fraction of low-coordinated surface Pt atoms which can be directly involved in the ORR process5-7. Herein, based on nitrogen-doped active carbon (Black Pearls 2000, denoted as NBP), a carbon-supported highly dispersed Pt nanocatalyst (Pt1@Pt/NBP) with low Pt content of 4.96 wt.% was prepared simply using a mild hydrothermal method. Results of electrochemical measurement and physical characterization reveal that, a large number of atomically dispersed Pt sites (Fig.1a) can remarkably enhance the ORR activity of Pt1@Pt/NBP electrocatalysts with a higher half-wave potential (E1/2 = 0.827 V) than that of Pt/BP (Fig.1b, E1/2 = 0.791 V) , commercial Pt/C (Fig.1c, E1/2 = 0.811 V) and the previously reported Pt1-N /BP catalysts6. This novel low-Pt electrocatalysts can be one of the promising alternatives to traditional Pt-based catalysts for the application in PEMFCs with its exceedingly improved Pt utilization and superhigh performance. Acknowledgements Work was funded by the national research foundation of Korea Grant, Korean government (MSIT) (NRF-2019M3D1A1079297) References (1)Steele, B. C. H.; Heinzel, A. Nature 2001, 414, 345. (2)Wang, Y.-J.; Zhao, N.; Fang, B.; Li, H.; Bi, X. T.; Wang, H. Chemical Reviews 2015, 115, 3433. (3)Stamenkovic, V. R.; Fowler, B.; Mun, B. S.; Wang, G.; Ross, P. N.; Lucas, C. A.; Markovic, N. M. Science 2007, 315, 493. (4)Huang, X.; Zhao, Z.; Cao, L.; Chen, Y.; Zhu, E.; Lin, Z.; Li, M.; Yan, A.; Zettl, A.; Wang, Y. M.; Duan, X.; Mueller, T.; Huang, Y. Science 2015, 348, 1230. (5)Cheng, H.; Cao, Z.; Chen, Z.; Zhao, M.; Xie, M.; Lyu, Z.; Zhu, Z.; Chi, M.; Xia, Y. Nano Letters 2019, 19, 4997. (6)Liu, J.; Jiao, M.; Lu, L.; Barkholtz, H. M.; Li, Y.; Wang, Y.; Jiang, L.; Wu, Z.; Liu, D.-j.; Zhuang, L.; Ma, C.; Zeng, J.; Zhang, B.; Su, D.; Song, P.; Xing, W.; Xu, W.; Wang, Y.; Jiang, Z.; Sun, G. nature commonications 2017, 8, 15938. (7)Zhang, H.; An, P.; Zhou, W.; Guan, B. Y.; Zhang, P.; Dong, J.; Lou, X. W. Science Advances 2018, 4, eaao6657. Figure 1