Isolation And Fractionation Of Hemicelluloses From Salix Psammophila
Feng Peng,Ning Jia,Jing Bian,Pai Peng,Feng Xu,Runcang Sun
2011-01-01
Cellulose Chemistry and Technology
Abstract:Water- and alkali-soluble hemicelluloses were isolated with hot water and 10% KOH at 25 degrees C from dewaxed and delignified Salix psammophila, respectively. The alkali-soluble hemicelluloses were then successively sub-fractioned by neutralization and graded precipitation at final ethanol concentrations of 15%, 30%, 45%, 60%, 75% and 90%, respectively. Chemical composition, physico-chemical properties, and structures of eight precipitated hemicellulosic fractions were elucidated by a combination of sugar analysis, molecular determination, FT-IR, H-1, C-13 2D HSQC NMR: It was found that water-soluble hemicelluloses were more branched, and had low molecular weights (6060 g/mol), whereas the alkali-soluble hemicelluloses were less branched, and had high molecular weights (17110-85540 g/mol), in which xylose and uronic acid are the main sugar component. In addition, the less branched hemicelluloses with large molecules were precipitated in lower ethanol percentages, while with the increasing ethanol concentrations, more branched hemicelluloses with low molecular weights were obtained. That is, linear hemicelluloses could be recovered at lower ethanol concentrations, and more branched hemicelluloses could be obtained at the higher ethanol concentrations. Based on the FT-IR, H-1, C-13 and 2D HSQC NMR studies, the alkali-soluble hemicelluloses had a main structure composed of the (1 -> 4)-linked beta-D-xylopyranosyl backbone with 4-O-methyl-alpha-D-glucuronic acid attached to O-2 of the xylose residues.