Abstract:In the process of promoting the commercialization of proton exchange membrane fuel cells, the long-term durability of the fuel cell has become a key consideration. While existing durability tests are critical for assessing cell performance, they are often time-consuming and do not quickly reflect the impact of actual operating conditions on the cell. In this study, improved testing protocols were utilized to solve this problem, which is designed to shorten the testing cycle and evaluate the degradation of the cell performance under real operating conditions more efficiently. Accelerated durability analysis for evaluating the MEA lifetime and performance decay process was carried out through two testing protocols—open circuit voltage (OCV)-based accelerated durability testing (ADT) and relative humidity (RH) cycling-based ADT. OCV-based ADT revealed that degradation owes to a combined mechanical and chemical process. RH cycling-based ADT shows that degradation comes from a mainly mechanical process. In situ fluoride release rate technology was employed to elucidate the degradation of the proton exchange membrane during the ADT. It was found that the proton exchange membrane suffered more serious damage under OCV-based ADT. The loss of F- after the durability test was up to 3.50 × 10−4 mol/L, which was 4.3 times that of the RH cycling-based ADT. In addition, the RH cycling-based ADT had a significant effect on the catalyst layer, and the electrochemically active surface area decreased by 48.6% at the end of the ADT. Moreover, it was observed that the agglomeration of the catalysts was more obvious than that of OCV-based ADT by transmission electron microscopy. It is worth noting that both testing protocols have no obvious influence on the gas diffusion layer, and the contact angle of gas diffusion layers does not change significantly. These findings contribute to understanding the degradation behavior of proton exchange membrane fuel cells under different working conditions, and also provide a scientific basis for developing more effective testing protocols.

Proton Exchange Membrane Fuel Cell (PEMFC) Durability Factors, Challenges, and Future Perspectives: A Detailed Review

Main factors affecting the lifetime of Proton Exchange Membrane fuel cells in vehicle applications: A review

A Review of Proton Exchange Membrane Degradation Pathways, Mechanisms, and Mitigation Strategies in a Fuel Cell

Recent Progress on the Key Materials and Components for Proton Exchange Membrane Fuel Cells in Vehicle Applications

Current status and future perspectives of proton exchange membranes for hydrogen fuel cells

Research Progress of Proton Exchange Membrane Failure and Mitigation Strategies

Catalytic Approaches Towards Highly Durable Proton Exchange Membrane Fuel Cells with Minimized Pt Use

A Review of Durability Test Protocols of the Proton Exchange Membrane Fuel Cells for Vehicle

Review on factors of voltage consistency and inconsistent degradation in proton exchange membrane fuel cells

Understanding the factors influencing the corrosion of bipolar plate to the performance and durability of unitized regenerative proton exchange membrane fuel cell: A review

Lifetime evaluation and material failure analysis of a PEMFC prepared using commercial materials

Review of hydrogen crossover through the polymer electrolyte membrane

Materials Engineering toward Durable Electrocatalysts for Proton Exchange Membrane Fuel Cells

A Comprehensive Review of Degradation Prediction Methods for an Automotive Proton Exchange Membrane Fuel Cell

Durability Test Of Pemfc With Pt-Pfsa Composite Membrane

Overcoming the Electrode Challenges of High-Temperature Proton Exchange Membrane Fuel Cells

VII.I.3 PEM Fuel Cell Durability

Key Components Degradation in Proton Exchange Membrane Fuel Cells: Unraveling Mechanisms through Accelerated Durability Testing

Analysis of proton exchange membranes for fuel cells based on statistical theory and data mining

A review on lifetime prediction of proton exchange membrane fuel cells system

Material degradation of components in polymer electrolyte membrane (PEM) electrolytic cell and mitigation mechanisms: A review