Abstract:As demand grows to replace petroleum-derived materials with more environmentally friendly materials, the use of wood in high-performance applications in the automotive industry has received increasing attention. Understanding the behaviour of wood during forming processes is an essential step towards its successful implementation in the automotive sector. This study accordingly investigates the compressive response and failure behaviour of two hardwood species (beech and birch) at different moisture and temperature levels. The experimental tests were conducted at 20, 60, 100 and 140 °C on samples with various moisture levels, ranging from completely dry to wet conditions. The stress–strain curves were analysed, and the failure modes were examined using visual observations and microscopic analyses. The results demonstrated that, when beech and birch were tested in standard laboratory conditions, the dominant mode of failure was the kink band, where the fibres buckled in an approximately sigmoidal shape. However, when the wet wood was tested at temperatures of 60 °C and above, the stress–strain curves showed long stress plateau region as well as strain hardening. We hypothesise that, at elevated moisture and temperature levels, the cell walls, promoted by the improved flexibility of the polymer network, start to fold, hence, the load stabilises or even slightly decreases. This corresponds to the plateau stage in the stress–strain curves of beech and birch. With further loading, the distance between the folds becomes rather small and compaction of the folds (or densification) apears to occur, corresponding to the observed strain–hardening stage. This hypothsis is supported by the concertina-like folds seen in the scanning electron microscope (SEM) graphs of post-tested specimens. Here, we present and discuss the effect of rays, as well as cell wall/lumen ratio, on the compression behaviour of wood, and the stability of the forming process.

High Strain Rate Compressive Tests on Wood

High-strain Rate Compressive Behavior of Douglas Fir and Glubam

Compressive Impact Tests of Lightweight Concrete with 155-Mm-diameter Spilt Hopkinson Pressure Bar

Compressive Behavior of Engineered Cementitious Composites under High Strain-Rate Loading

High-strain Rate Compressive Behavior of CFRP Confined Concrete: Large Diameter SHPB Tests

Experimental Studies on Concrete Filled Steel Tubes under High Strain Rate Loading

Challenges related to testing of composite materials at high strain rates using the split Hopkinson bar technique

Compressive Failure of Carbon/Epoxy Laminate Composites under High Impact Loading

Beyond Hopkinson's bar

A split Hopkinson bar technique for low-impedance materials

Dynamic Compressive Response and Failure Behaviour of CFRP Composites at High Strain Rates

Hopkinson bar experiments as a method to determine impact properties of brittle and ductile materials

Split Hopkinson pressure bar testing of 3D multi-axial warp knitted carbon/epoxy composites

Dynamic stress-strain curves for various plastics and fibre-reinforced plastics

Dynamic compressive impact behavior of CFRP composite under high strain rate loading

Compressive Split Hopkinson Pressure Bar Apparatus: Part I - Design and Development

Mechanical Behavior and Failure Mode of Woven Carbon/epoxy Laminate Composites under Dynamic Compressive Loading

Uniaxial Stress-Strain Behavior of Unsaturated Soils at High Strain Rates

The compressive behaviour of beech and birch at different moisture and temperature conditions along the grain

Effect of Strain Rate on the Transverse Tension and Compression Behavior of a Unidirectional Non-Crimp Fabric Carbon Fiber/Snap-Cure Epoxy Composite

Material characterization at high strain rate by Hopkinson bar tests and finite element optimization