Abstract:Magnetic nanoparticles and thin films exhibiting a large magnetic anisotropy energy density (MAE) have attracted enormous attention over the last years due to their potential use in magnetic data storage or sensing applications. FePt alloy nanoparticles and films have a huge MAE in the chemically ordered L10 phase. This ordered phase is typically obtained by annealing the as-prepared chemically disordered fcc FePt nanoparticles at temperatures above 600°C. Besides standard colloidal approaches [1], such fcc FePt nanoparticles can be fabricated by a micellar technique resulting in regular arrays on various substrates [2,3]. This approach offers the advantage that the interparticle distance can be tuned between 20-100 nm. Due to the larger separation particle agglomeration can be avoided during the annealing induced transformation into the L10 phase. Moreover, the particles are magnetostatically decoupled. We investigated the formation of the L10 phase for 2-10 nm FePt particles as a function of the annealing temperature and time on Si/SiOx substrates. Hysteresis loops at T = 15K reveal strongly enhanced coercive field after an annealing step at 700°C for 30 min compared to the as-prepared particles. The effective MAE is found to be 1-2×10 J/m using simple Stoner-Wohlfarth modeling that is a factor of 3-5 smaller than the FePt bulk MAE. In order to correlate the magnetic properties to the structure of the particles we performed transmission electron microscopy (TEM) investigations of FePt particles on both, Si/SiOx and MgO(001) substrates. Basically, the lowered MAE could originate from defective crystal structures, imperfect ordering of Feand Pt-planes (chemical ordering parameter), and/or inhomogeneous segregation of Fe/Pt within the particles. The applied TEM methods included conventional TEM (bright-field, dark-field, electron diffraction), spherical aberration corrected high resolution imaging and scanning TEM (Z-contrast). It was found that most particles contain defects such as stacking faults and multiple twins (Figure 1). Calculated TEM images based on various models of FePt nanoparticles (Figure 2) were generated and compared to experimental images especially to analyze and to determine the chemical ordering parameter of the L10 phase, crystal structure and defects.

Fabrication of surface magnetic nanoclusters using low energy ion implantation and electron beam annealing

On the magnetic properties of iron nanostructures fabricated via focused electron beam induced deposition and autocatalytic growth processes

Magnetic metamaterials by ion-implantation

Fabrication of magnetic clusters and rods using electrostatic co-assembly

Embedded Optical-Electrical Nanomateriales Fabricated By Ion Implantation

The growth of metastable fcc Fe78Ni22 thin films on H-Si(100) substrates suitable for focused ion beam direct magnetic patterning

A Novel Strategy for the Fabrication of High-Performance Nanostructured Ce-Fe-B Magnetic Materials Via Electron-Beam Exposure

Position Selective Introduction of Ferromagnetism on the Micro‐ and Nanoscale in a Paramagnetic Thin Palladium Film

Fabrication of Co/CoO Exchange Bias System by Ion Implantation and Its Magnetic Properties

Oxygen Implanted Ni/NiO Exchange Bias System: Fabrication, Structure and Magnetic Property.

Ion irradiation of Fe-Fe oxide core-shell nanocluster films: Effect of interface on stability of magnetic properties

Exploring the fabrication and transfer mechanism of metallic nanostructures on carbon nanomembranes via focused electron beam induced processing

ARTIFICIAL METAL NANOCLUSTER CRYSTALS

Fabrication and Characterization of Bonded NdFeB Microstructures for Microelectromechanical Systems Applications

Nanomagnetism of magnetoelectric granular thin-film antiferromagnets

Low-field microwave absorption and magnetoresistance in iron nanostructures grown by electrodeposition on n-type lightly-doped silicon substrates

Synthesis of ZnFe 2 O 4 Nanomagnets by Fe-ion Implantation into ZnO and Post-Annealing

Self-assembly of iron nanoclusters on the Fe3O4(111) superstructured surface

Atomic scale study of CU clustering and pseudo-homogeneous Fe-Si nanocrystallization in soft magnetic FeSiNbB(CU) alloys

Structural and Magnetic Investigations on FePt Nanoparticles