Abstract:This study was aimed to prepare a silk fibroin (SF)/chitosan (CS)/nano-Hydroxyapatite (n-HAp) composite scaffold for repair of cartilage damage. A four-layer bionic scaffold SF/CS/n-HAp was constructed by cryogenic freezing and forming. Sodium Tripolyphosphate (STPP) was used as a cross-linking agent to post-process the scaffold to improve the mechanical strength of the scaffold. The various materials prepared were characterized. The SF/CS/n-HAp scaffold prepared in this study was cream-colored cylindrical and elastic. It can show variability after external force was applied, and can be restored to its original appearance after elimination of the external force. The diameter of the scaffold was 5 cm, and the total thickness was about 1 cm. The scanning electron microscope (SEM) results showed that the surface of the scaffold material was smooth, the pore size changed gradually, and the connectivity among the holes was good. The pore size distribution of the entire scaffold material was between 100 μ m∼300 μ m, and the pore size range was suitable for the adhesion, expansion, and migration of chondrocytes and osteoblasts. The mechanical performance test results showed that the composite scaffold had a compression modulus of 706 kPa, which can meet the mechanical performance requirements for repair of smaller articular cartilage damage. In addition, the porosity of each layer of the scaffold was more than 91%, which was conducive to the adhesion of cells on the surface of the material. The cell experiment results revealed that the composite scaffold material was beneficial to the growth and proliferation of cells. Under osteogenic and chondrogenic induction culture, bone marrow stromal cells (BMSCs) can differentiate in the direction of osteogenesis and cartilage. The results of animal experiments revealed that the SF/CS/n-HAp material group showed better effect than the blank control group in repairing rat cartilage defects, and the Wayne score and O’Driscoll score were also significantly higher than the blank control group. This suggested that the biomimetic scaffold SF/CS/n-HAp prepared in this study showed good physical properties and biocompatibility, and had certain prospects in the application of repairing cartilage damage.

Repair of sports cartilage injury with tissue engineering scaffold material

Preparation of high precision multilayer scaffolds based on Melt Electro-Writing to repair cartilage injury

High-precision bioactive scaffold with dECM and extracellular vesicles targeting 4E-BP inhibition for cartilage injury repair

Tissue engineering strategies hold promise for the repair of articular cartilage injury

A composite scaffold of MSC affinity peptide-modified demineralized bone matrix particles and chitosan hydrogel for cartilage regeneration

3D-Printed Scaffolds with Calcified Layer for Osteochondral Tissue Engineering

Functional biomaterials for cartilage regeneration.

Enhanced osteochondral repair with hyaline cartilage formation using an extracellular matrix-inspired natural scaffold

Preparation of Silk Fibroin/Chitosan/Nano-Hydroxyapatite and Its Effect on the Repair of Cartilage Damage in Rats

Hyaluronic acid-based biphasic scaffold with layer-specific induction capacity for osteochondral defect regeneration

Tissue engineering and cartilage

Enhancing cartilage repair with optimized supramolecular hydrogel-based scaffold and pulsed electromagnetic field

Three-Dimensional Printed Silk Fibroin/Hyaluronic Acid Scaffold with Functionalized Modification Results in Excellent Mechanical Strength and Efficient Endogenous Cell Recruitment for Articular Cartilage Regeneration

Near-Field Direct Write Microfiber-Reinforced Collagen Hydrogel Scaffolds for Articular Cartilage Regeneration

Hydrogel composite scaffolds achieve recruitment and chondrogenesis in cartilage tissue engineering applications

Use of a biological reactor and platelet-rich plasma for the construction of tissue-engineered bone to repair articular cartilage defects

Demineralized bone matrix compounded with biological fibrin glue for repairing rabbit cartilage defects

Mechanism research on a bioactive resveratrol- PLA-gelatin porous nano-scaffold in promoting the repair of cartilage defect

Scaffold-Based Tissue Engineering Strategies for Osteochondral Repair

Structurally and Functionally Optimized Silk-Fibroin-Gelatin Scaffold Using 3D Printing to Repair Cartilage Injury In Vitro and In Vivo.

Recent strategies of collagen-based biomaterials for cartilage repair: from structure cognition to function endowment