Reduction of shrinkage of self compacting concrete using polycarboxylate ether as shrinkage reducing admixture

Shreyasee Sulakshna Sanjay,Apurba Pal,Sujit Kishor Chakraborty,Hasim Ali Khan

DOI: https://doi.org/10.1016/j.matpr.2022.01.316

2022-02-01

Materials Today: Proceedings

Abstract:The advancements in concrete and building technology have led to the demand for sustainable building materials over the last few decades. Various types of modified concrete like SCC or Self Compacting Concrete or Self Consolidated Concrete have also been developed and are considered as a new age highly modified concrete material. Self Compacting Concrete is considered a major evolution in the recent developments of the building industry. The semi-flow-able nature of SCC helps in construction and repair works along with several other advantages in terms of environmental, technological, economical and human. This work focuses on the effects of numerous types of shrinkage like drying shrinkage, plastic shrinkage and autogenous shrinkage on the performance of SCC. Many studies suggest that the excessive shrinkage properties in SCC provide a major hindrance to achieving the desired strength of the modified concrete. Capillary tension and expansive cracking are generally considered to be responsible for the shrinkage in SCC and lowering the water/cement ratio or reduction in filler/cement content leads to reduced levels of autogenous shrinkage. Cracks resulting from the excessive shrinkage are generally responsible for the substandard durability of the modified concrete as they provide spaces for hazardous fluids enter the concrete member resulting in an excessive plastic shrinkage. The effect of SRA or Shrinkage Reducing Admixtures is generally shown to have positive results and SRAs used in conjunction with compounds based on paraffin help in reduction of cracks. This paper also includes the experimental studies using Poly Carboxylate Ether (PCE) as SRA to combat the shrinkage of the modified concrete. This work included the use of poly carboxylate ether (PEC) over the use of commercially available shrinkage reducing admixtures (SRA) because it is locally available in many parts of the world where self compacting concrete has still not gained precedence over the normally vibrated concrete. The results obtained show that the use of PCE has similar effect to the lowering of shrinkage as the use of SRAs.